丙烯酸改性水性环氧酯树脂的合成研究  

Synthesis of Acrylic Modified Waterborne Epoxy Resin

作　　者：戴国绪 刘凤广 Dai Guoxu;Liu Fengguang(Changzhou Guangshu Chemical Technology Co.,Ltd.,Changzhou,Jiangsu 213000,China)

机构地区：[1]常州广树化工科技有限公司,江苏常州213000

出　　处：《涂层与防护》2020年第9期49-52,62,共5页Coating and Protection

摘　　要：本研究对环氧酯树脂进行改性,通过实验得出:当3#环氧树脂与5#环氧树脂的质量比为1∶1、环氧树脂与油酸的质量比为1.3∶1、亲水单体丙烯酸的用量为2.5%~3%时,制得的改性树脂所制涂料的涂膜综合性能最优。In this paper,the epoxy resin is modified.The experimental results show that the film derived from the modified resin has the best comprehensive performance when the ratio of 3#epoxy resin to 5#epoxy resin is 1:1,the mass ratio of epoxy resin to oleic acid is 1.3:1,and the amount of hydrophilic monomer acrylic acid is 2.5%-3%.

关 键 词：环氧酯树脂 丙烯酸酯 树脂改性 