利用工业废渣赤泥烧制高贝利特水泥的研究  

Study on firing high belite cement with red mud from industrial waste residue

作　　者：张忠伦 ZHANG Zhonglun(Central South University,Changsha 410083;CNBM Technology Innovation Academy(Shandong)Co.,Ltd.,Zaozhuang 277116)

机构地区：[1]中南大学,湖南长沙410083 [2]中建材科创新技术研究院(山东)有限公司,山东枣庄277116

出　　处：《中国建材科技》2020年第5期52-56,共5页China Building Materials Science & Technology

摘　　要：研究了利用铝工业废渣赤泥烧制高贝利特水泥(HBC)。结果表明,赤泥HBC熟料KH值的最优范围介于0.74~0.78,在此情况下,水泥的早后期强度都较高,且水泥需水量小、流动性好、易磨性较好。试验烧成的高贝利特水泥熟料28d强度≥42.5MPa,赤泥的利用率≥10%。This paper studies the firing of high belite cement(HBC)with alumnium industrial waste residue(red mud).The results show that the optimal range of KH of red mud HBC clinker is between 0.74 and 0.78.Under this condition,the cement has characteristics of high early and late compression strength,low water requirement,good fluidity and grindability.The 28d compression strength of HBC clinker in laboratory is more than 42.5 MPa,and the utilization rate of red mud is more than 10%.

关 键 词：赤泥 高贝利特水泥 工业废渣利用 