混炼工艺对防老剂RD残余量及胶料性能的影响  

Effect of Mixing Process on Residual Amount of Antioxidant RD and Properties of Compound

作　　者：董兴旺[1] 张小飞[1] 任福君[1] 叶李青[1] DONG Xingwang;ZHANG Xiaofei;REN Fujun;YE Liqing(Zhongce Rubber Group Co.,Ltd,Hangzhou 310018,China)

机构地区：[1]中策橡胶集团有限公司,浙江杭州310018

出　　处：《轮胎工业》2020年第10期614-617,共4页Tire Industry

摘　　要：研究混炼工艺对防老剂RD残余量及胶料性能的影响。结果表明:在高温处理过程中,防老剂RD发生分解反应,且随着热处理温度的升高,其质量损失增大;防老剂RD在高温(155℃)混炼阶段加入比在低温(110℃)混炼阶段加入质量损耗增大20%;与在高温混炼阶段加入相比,防老剂RD在低温混炼阶段加入,胶料在老化前的物理性能相当,但是在热老化后的物理性能、耐磨性能和抗切割性能等均得到改善。The effect of the mixing process on the residual amount of antioxidant RD and properties of the compound was investigated. The results showed that the antioxidant RD underwent decomposition reaction during the high temperature treatment,and its mass loss increased as the heat treatment temperature increased. When the antioxidant RD was added at a high temperature(155 ℃) stage,the mass loss was increased by 20% compared with that when it was added at a low temperature(110 ℃) stage. Compared with the addition in the high temperature mixing stage,the physical properties of the compound with antioxidant RD which was added in the low-temperature mixing stage were equivalent before heat aging,but the physical properties,wear resistance and cutting resistance after heat aging were improved.

关 键 词：防老剂 混炼工艺 老化 物理性能 耐磨性能 抗切割性能 

分 类 号：TQ330.382[化学工程—橡胶工业] TQ330.63