古彩颜料低铅熔剂的研究  

Study on Low Lead Frit of Paleo-color Pigments

作　　者：詹建平 李亚萍 张璞 刘萱 吴元发 ZHAN Jianping;LI Yaping;ZHANG Pu;LIU Xuan;WU Yuanfa(Ceramic Research Institute of Light Industry of China,Jingdezhen 333000,China;Gannan Normal University,Ganzhou 341000,China)

机构地区：[1]中国轻工业陶瓷研究所,景德镇333000 [2]赣南师范大学,赣州341000

出　　处：《中国陶瓷》2020年第11期77-82,共6页China Ceramics

摘　　要：采用多元系统,以碱金属、碱土金属氧化物以及氧化硼部分替代氧化铅,进行稳定低铅的古彩颜料熔剂的研究,讨论分析了铅含量、碱金属含量、Si/B比、Si/Al比等因素对低铅熔剂各项性能的影响。结果表明:古彩颜料熔剂的铅含量由50%~80%降低至25%以下,并具有良好的热稳定性、化学稳定性、光泽度和釉面质量。The paleo-color frit with low lead was studied by using multi-element system,replacing lead oxide with alkali metal,alkaline earth metal oxide and boron oxide,the effects of lead content,alkali metal content,Si/B ratio and Si/Al ratio on the properties of low lead frit are discussed and analyzed.The results showed that the lead content of the frit decreases from 50%~80%to less than 25%,and it has good thermal stability,chemical stability,glossiness and glaze quality.

关 键 词：古彩颜料 低铅熔剂 热稳定性 化学稳定性 光泽度 釉面质量 