7075-T6合金超声辅助搅拌摩擦焊接头搅拌区组织与力学性能  

Microstructure and Mechanical Properties of the Stirred Zone of Ultrasonic Assisted Friction Stir Welded Joint of 7075-T6 Alloy

作　　者：张志强 何长树 赵夙[3] 赵骧 ZHANG Zhi-qiang;HE Chang-shu;ZHAO Su;ZHAO Xiang(School of Materials Science&Engineering,Northeastern University,Shenyang 110819,China;Key Laboratory for Anisotropy and Texture of Materials,Northeastern University,Shenyang 110819,China;Ningbo Institute of Materials Technology&Engineering,Chinese Academy of Sciences,Ningbo 315201,China.)

机构地区：[1]东北大学材料科学与工程学院,辽宁沈阳110819 [2]东北大学材料各向异性与织构教育部重点实验室,辽宁沈阳110819 [3]中国科学院宁波材料技术与工程研究所,浙江宁波315201

出　　处：《东北大学学报（自然科学版）》2020年第12期1708-1714,共7页Journal of Northeastern University(Natural Science)

基　　金：国家重点研发计划项目(2016YFB1200506-12);兴辽英才计划项目(XLYC1808038).

摘　　要：搅拌区的金属流动不充分容易导致轴肩影响区与搅拌针影响区之间的过渡区出现疏松缺陷并恶化接头的力学性能.在不同焊接参数条件下,对7075-T6铝合金分别进行常规搅拌摩擦焊接(FSW)和超声辅助搅拌摩擦焊接(UAFSW),研究了超声振动对接头搅拌区的金属流动行为、微观组织特征和力学性能的影响.结果表明:相同焊接参数下,UAFSW接头搅拌区的力学性能均优于FSW接头.焊接参数为1000 r/min-110 mm/min的UAFSW接头搅拌区的抗拉强度和延伸率最高,分别达到515 MPa和17.3%.在搅拌摩擦焊接过程中施加轴向超声振动可以显著降低搅拌区金属的屈服应力和流变应力,促进塑化金属沿板厚方向的流动.消除搅拌区中过渡区的疏松缺陷,并细化微观组织,是接头力学性能提高的主要原因.Insufficient metal flow in the stirred zone(SZ)may easily lead to loose defects in the transition zone between the shoulder-affected zone and the pin-affected zone,and deteriorate the mechanical properties of the joint.7075-T6 aluminum alloy was subjected to conventional friction stir welding(FSW)and ultrasonic assisted friction stir welding(UAFSW)under different welding parameters,and the effects of ultrasonic vibration on the metal flow behavior,microstructure characteristics and mechanical properties of the SZ were investigated.The results show that the mechanical properties of the SZ of UAFSW joints are better than that of FSW joints processed using the same welding parameters.Tensile strength and elongation of the SZ of UAFSW joint with the welding parameters of 1000 r/min-110 mm/min reach the maximum values,i.e.515 MPa and 17.3%,respectively.The application of axial ultrasonic vibration during FSW can significantly reduce yield stress and flow stress of the metal in the SZ,promoting the flow of plasticized metal along the normal direction of the plate.Eliminating the loose defects in the transition zone of the SZ and refining the microstructure are the main reasons for improving the mechanical properties of the joint.

关 键 词：超声辅助搅拌摩擦焊 铝合金 搅拌区 显微组织 力学性能 

分 类 号：TG146.2[一般工业技术—材料科学与工程]