Effect of TiO2 on reduction behavior of Cr2O3 in CaO-SiO2-Al2O3-MgO-TiO2-Cr2O3 by carbon from Fe-C melt  

作　　者：Jun-yi Xiang Gui-shang Pei Wei Lv Bao-hua Li Gui-bao Qiu Xue-wei Lv 

机构地区：[1]College of Materials Science and Engineering,Chongqing University,Chongqing 400044,China [2]Chongqing Key Laboratory of Vanadium-Titanium Metallurgy and Advanced Materials,Chongqing University,Chongqing 400044,China

出　　处：《Journal of Iron and Steel Research International》2020年第10期1145-1152,共8页

基　　金：supported by the project funded by China Postdoctoral Science Foundation(Grant No.2018M640898);the National Key Research and Development Program of China(2018YFC1900500);the National Natural Science Foundation of China(No.51674055);the open project funded by State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization.

摘　　要：The chromium-bearing titanomagnetite ore will turn to be the important raw material for blast furnace process in Panxi area,China.The reduction behavior of Cr2O3 between CaO-SiO2-Al2O3-TiO2-Cr2O3 and Fe-C systems was investigated.The effect of TiO2 content in the slag system on the reduction of Cr2O3,TiO2,and SiO2 and the con sumption of C in hot metal was investigated by both theoretical calculation and physical experiment.The theoretical calculation results reveal that higher reduction temperature promotes the reduction of Cr and Ti,while high basicity and TiO2 content have little influence on the reduction of chromium but significantly influence the reduction of Ti.The smelting reduction experiment results show that the content of Cr in hot metal significantly in creases with extendi ng the reduction time and decreases with the increase in TiO2 content.However,the content of Ti in hot metal significantly increases as the TiO2 increases,reaching 0.073,0.085,0.107,and 0.121 wt.%for 5,10,15,and 20 wt.%of TiO2 input,respectively.Kinetic studies proved that the reduction of Cr2O3 was a first-order reaction.The addition of TiO2 inhibited the reduction of Cr2O3 and resulted in the decrease in reaction rate constant.

关 键 词：Smelting reduction TITANOMAGNETITE Blast furnace slag Chromium oxide Titanium oxide 