Recovery of zinc from Zn-Al-Fe alloys by gas pressure filtration  

作　　者：Tian-yang Li Zhe Wang Lei Guo Zhan-cheng Guo 

机构地区：[1]State Key Laboratory of Advanced Metallurgy,University of Science and Technology Beijing,Beijing 100083,China

出　　处：《Journal of Iron and Steel Research International》2020年第11期1322-1330,共9页

基　　金：the National Natural Science Foundation of China(No.51704022);the Fundamental Research Funds for the Central Universities(FRF-TP-19-010A2).

摘　　要：The recovery of zinc from galvanizing dross and the removal of iron contained dross particles by gas pressure filtration were investigated using the model of Zn-Fe-Al alloys.The majority of molten zinc was separated after filtration,and the residue intercepted by the filter consisting mostly of dross particles.The effects of the pressure differential(p),separation temperature(T)and alloy composition on the zinc recovery and iron removal were investigated.At p=0.30 MPa and T=723 K,86.2 wt.%zinc was recovered from the Zn-4Al-2Fe alloy,and up to 99.9 wt.%of the iron was concentrated in the residue.Applying a higher pressure differential led to the improved filtration efficiency,and the desired separation temperature was about 723 K.The aluminum content in the Zn-Al-Fe alloy had little effect on separation efficiency,whereas increasing the iron content led to a decrease in the separation efficiency.Our findings demonstrate the potential of the gas pressure filtration method for the recovery of zinc from galvanizing dross.

关 键 词：Galvanizing dross Gas pressure filtration Zinc recovery Iron removal SEPARATION 