锰源粉末对Fe-Mn-C烧结钢组织和力学性能的影响  

Effect of manganese source powders on microstructure and mechanical properties of Fe-Mn-C sintered steel

作　　者：胡明 杨英杰 李普明 袁勇 张德金 于永亮 李松林[1] HU Ming;YANG Ying-jie;LI Pu-ming;YUAN Yong;ZHANG De-jin;YU Yong-liang;LI Song-lin(Powder Metallurgy Research Institute,Central South University,Changsha 410083,China;Powder Metallurgy Co.,Ltd.,Laiwu lron and Steel Group,Laiwu 271105,China)

机构地区：[1]中南大学粉末冶金研究院,长沙410083 [2]莱芜钢铁集团粉末冶金有限公司,莱芜271105

出　　处：《粉末冶金技术》2020年第6期403-408,共6页Powder Metallurgy Technology

摘　　要：以电解锰粉和Fe-76%Mn粉末(质量分数)为原料,在600℃和70%N2+30%H2混合气体(体积分数)管式炉中氮化得到三种抗氧化含氮锰源粉末(Mn-3%N、Mn-5%N和FeMn-3%N,质量分数),研究锰含量以及锰源粉末种类对压制烧结Fe-Mn-C烧结钢组织和力学性能的影响。研究表明:使用氮化锰源粉末制备的Fe-Mn-C烧结钢的力学性能明显优于采用电解锰粉为原料制备的同类材料,随着锰源粉末中N含量的升高,烧结钢烧结膨胀率减小,对合金的强化作用增加。以Mn-5%N作为锰源制备的Fe-2Mn-0.5C烧结钢,其拉伸强度为576 MPa,断后延伸率为3.8%,与电解锰粉为锰源相比,烧结钢的拉伸强度和断后延伸率分别提升了29%和123%。使用氮化锰粉作为锰源的烧结钢内孔隙数量减小,珠光体增多,片层间距降低。Using the electrolytic manganese powders and Fe-76%Mn powders(mass fraction)as the raw materials,the antioxidative nitrogen-manganese source powders(Mn-3%N,Mn-5%N,and FeMn-3%N,mass fraction)were prepared in the tube furnace with 70%N2+30%H2 gas(volume fraction)at 600℃,the effects of the manganese mass fraction and the type of manganese source powders on the microstructure and mechanical properties of the Fe-Mn-C sintered steels were investigated.In the results,the mechanical properties of the Fe-Mn-C sintered steels prepared by the nitrogen-manganese source powders are obviously better than those prepared by the electrolytic manganese powders.With the increase of the nitrogen mass fraction in the manganese source powders,the sintering expansion rate of the sintered steels decreases,and the strengthening of the Fe-Mn-C alloy is increased.The tensile strength of the Fe-2Mn-0.5C sintered steels prepared by Mn-5%N powders is 576 MPa,and the fracture elongation is 3.8%,which is improved by 29%and 123%,respectively,compared with those prepared by the electrolytic manganese powders.The number of pores in the sintered steels prepared by the nitrogen-manganese source powders decreases,the pearlite increases,and the lamellar spacing decreases.

关 键 词：烧结钢 锰粉 氮化 力学性能 显微组织 

分 类 号：TG142.1[一般工业技术—材料科学与工程]