Spectroscopic investigations on Yb^3+ doped and Pr^3+/Yb^3+ codoped tellurite glasses for photonic applications  

作　　者：M.Seshadri M.J.V.Bell V.Anjos Y.Messaddeq 

机构地区：[1]Grupo de Engenharia e Espectroscopia de Materiais,Departamento de Fisica-ICE,Universidade Federal de Juiz de Fora,Juiz de Fora,MG,36036-900,Brazil [2]Centre d'Optique,Photonique et Laser,2375 Rue de la Terrasse,Universite Laval,Quebec,QC,G1V 0A6,Canada

出　　处：《Journal of Rare Earths》2021年第1期33-42,I0002,共11页稀土学报（英文版）

基　　金：Project supported by Programa Nacional de Pos-Doutorado(PNPD/CAPES-086/2013)-Brazil。

摘　　要：In this work we repo rt on structural and spect roscopic properties of Yb^3+doped and Pr^3+/Yb^3+co-doped TeO2-Bi2 O3-ZnO-Li2 O-Nb2 O5(TBZLN)tellurite glasses.Bending and stretching modes of TeO2 and Te-OH bond(strong and weak)were analysed from the deconvolution of observed Raman and FT-IR spectra.Based on the absorption measurements,the energy bands of Yb^3+and Pr^3+ions are assigned.The spectroscopic properties for the radiative transitions of Yb^3+and Pr^3+ions were reported using McCumber and Judd-Ofelt theories.Visible emission bands originating from 3 P1 and 3 P0 to lower lying levels of Pr^3+were registered under 447 nm excitation.The emission band around 1334 nm assigned to the Pr3:1 G4→3 H5 was observed when excited at 980 nm.The stimulated emission cross-section(σemi(λ))and effective linewidth(Δλeff)for the 3 P1→3 H6,3 P1→3 H5,3 P0→3 H6,3 P0→3 F2,3 P1→3 F3,3 P1→3 F4,3 P0→3 F4 and 1 G4→3 H5 transitions of Pr^3+are reported.Upconversion luminescence in Pr^3+/Yb^3+codoped glass upon 980 nm excitation was measured.Possible resonant transfer processes between Yb^3+and Pr^3+ions are presented and discussed.The chromaticity co-ordinates were also evaluated from the visible emission spectra showing that Pr^3+/Yb^3+co-doped glass may be suitable for the development of yellow-orange(λexc=447 nm)and near white light(λexc=980 nm)emitting devices in photonics.

关 键 词：Rare earth ions Tellurite glass Spectroscopic properties Upconversion luminescence 