Wear and mechanical properties of carburized AISI 8620 steel produced by powder metallurgy  

作　　者：Mehmet Akif Erden Fatih Aydın 

机构地区：[1]Department of Biomedical Engineering,Karabuk University,Karabuk 78050,Turkey [2]Department of Metallurgical and Materials Engineering,Karabuk University,Karabuk 78050,Turkey

出　　处：《International Journal of Minerals,Metallurgy and Materials》2021年第3期430-439,共10页矿物冶金与材料学报（英文版）

摘　　要：The effect of carburization on the tensile strength and wear resistance of AISI 8620 steel produced via powder metallurgy was investigated.Alloys 1 and 2(with 0.2wt%C and 0.25wt%C,respectively)were first pressed at 700 MPa and then sintered at 1300,1400,or 1500℃for 1 h.The ideal sintering temperature of 1400℃was determined.Afterward,Alloys 1 and 2 sintered at 1400℃were carburized at 925℃for 4 h.The microstructure characterization of alloys was performed via optical microscopy and scanning electron microscopy.The mechanical and wear behavior of carburized and noncarburized alloys were investigated via hardness,tensile,and wear tests.After carburization,the ultimate tensile strength of Alloys 1 and 2 increased to 134.4%and 138.1%,respectively.However,the elongation rate of Alloys 1 and 2 decreased to 62.6%and 64.7%,respectively.The wear depth values of Alloy 2 under noncarburized and carburized conditions and a load of 30 N were 231.2 and 100.1μm,respectively.Oxidative wear changed to abrasive wear when the load transitioned from 15 to 30 N.

关 键 词：powder metallurgy steels CARBURIZATION microstructure WEAR mechanical properties 

分 类 号：TG142.1[一般工业技术—材料科学与工程]