Thermodynamic descriptions of quaternary Mg-Al-Zn-Bi system supported by experiments and their application in descriptions of solidification behavior in Bi-additional AZ casting alloys  

作　　者：Ying Tang Yongsheng Li Weimin Zhao Irina Roslyakova Lijun Zhang 

机构地区：[1]School of Materials Science and Engineering.Hebei University of Technology,Tianjin 300130,PR China [2]ICAMS,Ruhr-Universitat Bochum,Universitdtsstrasse150,44801 Bochum,Germany [3]State Key Laboratory of Powder Metallurgy,Central South University,Changsha 410083,PR China

出　　处：《Journal of Magnesium and Alloys》2020年第4期1238-1252,共15页镁合金学报（英文）

基　　金：The financial support from Hebei Provincial Science and Technology Program of China(Grant no.E2019202234);Research Foundation from Education Department of Hebei Province(Grant no.BJ2018026)-Outstanding Young Talents Plan is acknowledged.

摘　　要：16 Mg-Al-Zn-Bi quaternary alloys were utilized to measure the phase equilibria and transformation temperatures in the Mg-rich Mg-Al-Zn-Bi quaternary system by means of the X-ray diffraction,electron probe micro-analysis and differential scanning calorimetry techniques.The isothermal section at 400℃and three vertical sections along Mg-8 wt%Al-0.75 wt%Zn-vBi,Mg-3.4 wt%Al-0.5 wt%Zn-ABi and Mg-6.9 wt%Al-2.3 wt%Zn-xBi in the Mg-Al-Zn-Bi quaternary system were constructed.Based on the literature data,the ternary Mg-Al-Bi and Mg-Bi-Zn systems were re-assessed using the CALculaiton of PHAse Diagram(CALPHAD)approach.The calculated phase equilibria agree well with the measured data.By directly extrapolating the constituent sub-ternary systems,the thermodynamic database for the Mg-Al-Zn-Bi quaternary system was developed.The remarkable consistency between the predicted phase equilibria and the presently measured data in Mg-Al-Zn-Bi quaternary system further demonstrated the accuracy and reliability of the established thermodynamic database.After that,by using the newly developed thermodynamic database,the growth restrict factors and the solidification curves in Bi-containing AZ series magnesium alloys were calculated and analyzed.It was confirmed that the grain size of AZ alloys can be refined with the addition of Bi,and the comp on ent Al had larger grain refinement effect than Bi.Besides,the amount of Bi had also no ticeable effect on the solidification sequence of the AZ alloys.

关 键 词：Mg-Al-Zn-Bi quaternary system Phase equilibira CALPHAD Thermodynamics Solidification behavior. 

分 类 号：TG146.22[一般工业技术—材料科学与工程]