SnO_(2)含量对AgCuOSnO_(2)电接触性能的影响  

Influence of SnO_(2)Content on AgCuOSnO_(2)Electrical Contact Performance

作　　者：杨敏杰[1,2] 刘满门 姚芳 李晓龙 周晓龙[1,2] Yang Minjie;Liu Manmen;Yao Fang;Li Xiaolong;Zhou Xiaolong(College of Materials Science and Technology,Kunming University of Science and Technology,Kunming 650093,China;Key Laboratory of Advanced Materials of Yunnan Province/Key Laboratory of Advanced Materials in Rare&Precious and Nonferrous Metals,Ministry of Education,Kunming 650093,China;State Key Laboratory of Rare Precious Metals Comprehensive Utilization of New Technologies,Kunming 650106,China)

机构地区：[1]昆明理工大学材料科学与工程,云南昆明650093 [2]云南省先进材料重点实验室/稀贵及有色金属先进材料教育部重点实验室,云南昆明650093 [3]稀贵金属综合利用新技术国家重点实验室,云南昆明650106

出　　处：《稀有金属材料与工程》2021年第1期63-70,共8页Rare Metal Materials and Engineering

基　　金：Key Project of Yunnan Province Science and Technology Program of China(2017FA027);the Natural National Science Foundation of China(51361016)。

摘　　要：采用反应合成法制备了不同SnO_(2)含量的AgCuOSnO_(2)电接触材料。采用FQR-7501型涡流电导率仪测量抛光AgCuOSnO_(2)的电导率。用扫描电镜(SEM)观察和研究了AgCuOSnO_(2)电接触表面的侵蚀形貌。JF04C直流数字电阻测试仪用于进行10000点测试。结果表明,AgCuO(10)SnO_(2)(5)和AgCuO(10)SnO_(2)(8)电触头材料在U=12 V和I=15 A时的接触电阻小于1.3 mΩ,波动最小;当I=10 A时,AgCuO(10)SnO_(2)(x)(x=2,5,8)的熔焊力小于8 cN,AgCuO(10)SnO_(2)(5)电触头的熔焊力较小,当电流增大时熔焊力较为稳定;当AgCuOSnO_(2)电触头材料发生电弧侵蚀时,材料从阳极向阴极转移。随着SnO_(2)含量的增加,材料传输过程中的损耗得到抑制和降低。所转移的电触头表面有少量的气孔和微裂纹,表面形貌较为平坦。AgCuOSnO_(2)electrical contact materials with different SnO_(2)contents were prepared by reaction synthesis.FQR-7501 eddy current conductivity meter was used to measure the conductivity of the polished AgCuOSnO_(2).The erosion morphology of the surface of the AgCuOSnO_(2)electrical contact was observed by scanning electron microscope(SEM).The JF04C DC digital resistance tester was used to carry out 10000 dot tests.The results show that the contact resistance of AgCuO(10)SnO_(2)(5)and AgCuO(10)SnO_(2)(8)electric contact materials is lower than 1.3 mΩat U=12 V and I=15 A,and the fluctuation is the smallest;when I=10 A,the welding force of AgCuO(10)SnO_(2)(x)(x=2,5,8,%,mass fraction)is less than 8 cN,and the welding force of AgCuO(10)SnO_(2)(5)electric contact is small and stable when the current increases;when the arc erosion of AgCuOSnO_(2)electric contact materials occurs,the material transfer way is from anode to cathode.With the increasing of SnO_(2)content,the loss in the process of material transfer is restrained and reduced.There are a few pores and microcracks on the surface of the transferred electrical contact,and the surface morphology is relatively flat.

关 键 词：AgCuOSnO_(2)电接触材料 电接触性能 电弧侵蚀形貌 