变压器铅黄铜线夹开裂原因分析  

Analysis on Cracking of Lead Brass Clamp for Transformer

作　　者：郑宏晔 陈胤桢 裘吕超 周桢 邹君文 ZHENG Hongye;CHEN Yinzhen;QIU Lyuchao;ZHOU Zhen;ZOU Junwen(Electric Power Research Institute,State Grid Zhejiang Electric Power Co.,Ltd.,Hangzhou 310014,Zhejiang China;Zhejiang Electric Power Boiler&Pressure Vessel Inspection Institute Co.,Ltd.,Hangzhou 310014,Zhejiang China)

机构地区：[1]国网浙江省电力有限公司电力科学研究院,浙江杭州310014 [2]浙江省电力锅炉压力容器检验所有限公司,浙江杭州310014

出　　处：《热处理》2021年第1期51-53,共3页Heat Treatment

摘　　要：一变压器铅黄铜线夹使用了约10年时发生开裂。对开裂的线夹进行了宏观检查、化学成分分析、金相检验、断口分析及能谱分析。结果表明:线夹的化学成分和显微组织基本正常,但发生了应力腐蚀,并伴随有脱锌现象,从而导致其开裂。A transformer clamp made of lead brass cracked when used for about 10 years.Macro-check,chemical composition analysis,metallographic examination,fracture testing,and energy dispersive spectrum(EDS)analysis were carried out for the cracked clamp.The result showed that the clamp exhibited basically allowable chemical composition and microstructure but undesired stress corrosion,and was accompanied with dezincification,thus resulting in its cracking.

关 键 词：铅黄铜线夹 应力腐蚀 脱锌 

分 类 号：TG174.4[金属学及工艺—金属表面处理]