中薄板坯连铸机板间漏钢的原因分析及控制措施  

Cause Analysis and Control Measures of Steel Leakage in Medium-thin Slab Caster

作　　者：刘鑫 王帅 赵建平 吴志杰 金玉 LIU Xin;WANG Shuai;ZHAO Jianping;WU Zhijie;JIN Yu(Tangshan Iron and Steel Company,Hebei Iron and Steel Group Co.,Ltd.,Tangshan 063016,China)

机构地区：[1]河钢集团唐钢公司,河北唐山063016

出　　处：《铸造技术》2021年第3期207-210,共4页Foundry Technology

摘　　要：对中薄板坯连铸机板间漏钢的原因进行了分析。结果表明,造成板间漏钢的主要原因是水口面氧化。通过优化水口面材质、提高水口面精度、改进水口烘烤工艺,确保上下水口对中、氩气压力在0.01 MPa以上,提高快换机构液压缸速度、保证快换机构的精度和冷却效果,规范快换浸入式水口操作等措施,可以使中薄板坯连铸机无板间漏钢。The reason of steel leakage between plate in medium-thin slab caster was analyzed.The results show that the main cause of steel leakage between plates is oxidation of nozzle surface.By optimizing the nozzle surface material,to improve the nozzle surface accuracy,to improve the slide baking process,to ensure that the gate on the up and down,argon gas pressure above 0.01 MPa,to improve the quick change institutions hydraulic cylinder speed and guarantee the accuracy of the quick change and cooling effect,fast in submerged nozzle measures such as operation,it can make in the thin slab continuous caster without plate between the steel.

关 键 词：中薄板坯连铸机 浸入式水口 水口面 板间漏钢 

分 类 号：TG243[金属学及工艺—铸造]