Mechanical properties and microstructure of in situ formed Ti_(2)AlN/TiAl(WMS)composites  

作　　者：Wan-Liang Liang Rui Hu Yi-Wen Liu Tie-Bang Zhang Jin-Shan Li 

机构地区：[1]State Key Laboratory of Solidification Processing,Northwestern Polytechnical University,Xi'an 710072,China

出　　处：《Rare Metals》2021年第1期190-194,共5页稀有金属（英文版）

基　　金：financially supported by the National Basic Research Program of China(No.2011CB605503);the Program of Introducing Talents of Discipline to Universities(No.B08040)。

摘　　要：The Ti_(2)AlN-reinforced TiAl(WMS)composites with different contents of Ti_(2)AlN were prepared by an in situ method of reactive arc-melting technique.According to the results of X-ray diffraction(XRD)analysis,the Ti_(2)AlNreinforced WMS composites consist ofγ-TiAl,α_(2)-Ti_(3)Al,and Ti_(2)AlN phases.Microstructure analysis results indicate that Ti_(2)AlN reinforcements with rod-like in shape form in the WMS matrix with aα_(2)/γlamellar structure containing some bulk y phases.With volume fraction of Ti_(2)AlN increasing,the grain size of the composites decreases significantly and the elasticity modulus(E)increases.The compressive strength and compressive fracture strain of the composite with 3 vol%Ti_(2)AlN have a maximum value of 1,654 MPa and 22.5%,respectively,which are approximately improved by 45.84%and 29.31%,respectively,compared with that of the unreinforced WMS alloy.

关 键 词：Ti_(2)AlN/TiAl(WMS)composites Reactive arc-melting MICROSTRUCTURE Compressive properties 

分 类 号：TB33[一般工业技术—材料科学与工程]