2205双相不锈钢中σ相析出的影响因素分析  

Analysis of influencing factors of σ phase precipitation in 2205 duplex stainless steel

作　　者：刘燕 高仁强 陈兴润[2] 钱张信[2] Liu Yan;Gao Renqiang;Chen Xingnun;Qian Zhangxin(Technology Center,Jiuquan Iron and Steel Group Corporation,Jiayuguan Gansu 735100,China;Hongxing Iron and Steel Co.,Ld.,Jiuquan lron and Steel Group Corporation,Jiayuguan Gansu 735100,China)

机构地区：[1]酒钢集团技术中心,甘肃嘉峪关735100 [2]酒钢集团宏兴钢铁股份有限公司,甘肃嘉峪关735100

出　　处：《金属热处理》2021年第3期180-183,共4页Heat Treatment of Metals

摘　　要：分析了时效温度、时效时间、固溶温度、铬和钼含量对2205双相不锈钢中σ相析出量的影响规律。结果表明:随着时效时间延长,σ相析出量依次增加。在相同的时效时间下,随着时效温度升高σ相含量依次增大,在850℃时达到最大值;温度超过850℃后,随着时效温度升高σ相含量依次减小。时效时间相同的情况下,随着固溶温度、铬含量和钼含量升高,σ相析出时间变短、析出量增加。Effects of aging temperature,aging time,solution temperature,Mn and Mo content on the precipitation quantity ofσphase in 2205 duplex stainless steel were analyzed.The results show that with the aging time increasing,the precipitation amount ofσphase increases.At the same aging time,the content ofσphase increases with the increase of aging temperature.The precipitation quantity ofσphase is largest when aged at 850℃.When the temperature exceeds 850℃,the quantity of theσphase decreases with temperature increasing.Increasing the solution temperature,Cr content and Mo content can make precipitation time shorten and the precipitation quantity increase at the same aging time.

关 键 词：2205双相不锈钢 时效 Σ相 铬含量 钼含量 

分 类 号：TG156.92[金属学及工艺—热处理]