Low-temperature molten salt synthesis and luminescence properties of Eu(Ⅲ)-based coordination polymer nanosheets  

作　　者：Lei Wang Hao Liu Shuang Huang Sheng-Liang Zhong 

机构地区：[1]College of Chemistry and Chemical Engineering,Jiangxi Normal University,Nanchang 330022,China

出　　处：《Rare Metals》2021年第3期728-735,共8页稀有金属（英文版）

基　　金：financially supported by the National Natural Science Foundation of China(Nos.21301078 and21261010);Jiangxi Provincial Education Department(No.GJJ13215);the Sponsored Program for Cultivating Youths of Outstanding Ability in Jiangxi Normal University;the Initial Fund for Doctors from Jiangxi Normal University;Youth Foundation of Jiangxi Normal University;Postdoctoral Scientific Research Foundation of Jiangxi Normal University;Scientific Research Foundation of Graduate School of Jiangxi Normal University(No.YJS2015017)。

摘　　要：In this work,Eu(III)-based coordination polymer(EuCP) nanosheets were successfully synthesized using tetrabutylammonium bromide(TBAB) as low-temperature molten salt(LMS),terephthalic acid(PTA) and pyromellitic acid(PMA) as organic building blocks at 160℃.X-ray diffraction(XRD),Fourier transform infrared(FTIR),scanning electron microscopy(SEM),transmission electron microscopy(TEM) and thermogravimetry and differential thermal analysis(TG-DTA) were used to characterize the obtained products.Results show that the nanosheets have an average size of 200 nm and a thickness of about 50 nm.The effect of reaction temperature,reaction time and molar ratio of Eu^(3+)/PTA/PMA on the preparation was investigated.It turns out that all of them have great effect on morphology and size of the final product.When excited with 315 nm,strong emission centering at 617 nm is realized.Importantly,this synthetic methodology may offer a new alternative in the preparation of rare earth nanomaterials.

关 键 词：Molten salt Coordination polymer Rare earth NANOSHEETS 