液体聚丁二烯对溶聚丁苯橡胶/顺丁橡胶并用胶胎面性能的影响  

Effect of LPBD on the property of SSBR/BR blend tread compound

作　　者：刘紫妍 韩流 涂杰昀 刘迪[1] 雍占福 LIU Ziyan;HAN Liu;TU Jieyun;LIU Di;YONG Zhanfu(Key Laboratory of Rubber-Plastics of Ministry of Education,Shandong Provincial Key Laboratory of Rubber-Plastics,Qingdao University of Science&Technology,Qingdao 266042,China)

机构地区：[1]青岛科技大学,橡塑材料与工程教育部重点实验室,山东省橡塑材料与工程重点实验室,山东青岛266042

出　　处：《弹性体》2021年第2期1-5,共5页China Elastomerics

基　　金：国家自然科学基金项目(51972185)。

摘　　要：考察了3种牌号液体聚丁二烯(LPBD)取代芳烃油及不同硫磺用量对溶聚丁苯橡胶(SSBR)/顺丁橡胶(BR)并用胎面胶填料分散、物理机械性能及动态力学性能的影响。结果表明,添加3种牌号LPBD后,混炼胶的Payne效应减弱,均改善了补强填料的分散效果;硫化胶的拉伸强度、撕裂强度、耐磨性能均有提高;在相同硫磺用量下,LPBD-AL与芳烃油混合填充的并用胎面胶的抗湿滑性能基本不变,而LPBD-PM4、LPBD-N4-5000与芳烃油混合填充的并用胎面胶的抗湿滑性能稍有下降;在LPBD-AL与芳烃油混合填充的情况下,增加硫磺用量,tanδ(0℃)增大,胎面抗湿滑性能明显提升,tanδ(60℃)小幅降低,滚动阻力略有降低,胎面胶综合性能提升。The effects of three brands of liquid polybutadiene(LPBD)substituted aromatics oil and different sulfur content on the filler dispersion,physical and mechanical properties and dynamic mechanical properties of solution polymerized styrene-butadiene rubber(SSBR)and cis-polybutadiene rubber(BR)were investigated.The results showed that the three LPBD brands all improved the dispersion effect of the reinforcing filler.The Payne effect of the compound was weakened.The tensile strength and tearing strength of vulcanized rubber increased and the abrasion loss decreased.At the same sulfur content,compared with the mixed binder filled with aromatic oil,the wet skid resistance of the mixed binder filled with LPBD-AL and aromatic oil remained basically unchanged,while the wet skid resistance of the mixed binder filled with LPBD-PM4 and N4-5000 and aromatic oil decreased slightly.In the case of mixing LPBD-AL and aromatic oil to fill,increasing the amount of sulfur,tanδat 0℃increased,and the wet skid resistance of the tread was obviously improved;tanδat 60℃decreased slightly,and the rolling resistance slightly reduced.The comprehensive performance of tire tread was improved.

关 键 词：溶聚丁苯橡胶 顺丁橡胶 液体聚丁二烯 增塑剂 抗湿滑性 

分 类 号：TQ336.1[化学工程—橡胶工业]