热变形参数对316L/Q370qE复合板结合强度的影响  

Influence of hot deformation parameters on bonding strength of 316L/Q370qE clad plate

作　　者：邵春娟 镇凡 曲锦波 雒广杰 Shao Chunjuan;Zhen Fan;Qu Jinbo;Luo Guangjie(Institute of Research of Iron and Steel,Jiangsu Shagang Group Co.,Ltd.,Zhangjiagang Jiangsu 215625,China;Steel Plate Plant,Jiangsu Shagang Group Co.,Ltd.,Zhangjiagang Jiangsu 215625,China)

机构地区：[1]江苏省(沙钢)钢铁研究院,江苏张家港215625 [2]江苏沙钢集团有限公司钢板总厂,江苏张家港215625

出　　处：《金属热处理》2021年第5期132-137,共6页Heat Treatment of Metals

摘　　要：通过Gleeble-3800热压缩试验模拟316L/Q370qE复合板轧制,并借助拉伸试验、硬度试验、组织分析等手段,研究了变形量、变形温度、变形前保温时间等参数对界面结合强度的影响规律。结果表明:随着变形量的增加,结合强度逐渐升高,变形量大于20%时,结合强度升高趋势变缓;随着变形温度的升高,结合强度先升高后降低,1100℃与1250℃时结合强度相差不大;随着保温时间的延长,结合强度逐渐降低。Rolling process of the 316 L/Q370 qE clad plate was simulated by Gleeble-3800 thermal compression testing.And the influence of deformation amount,deformation temperature and holding time before deformation on bonding strength of the clad plate was studied by means of tensile testing,hardness testing and microstructure analysis.The results show that the bonding strength gradually increases with the increase of deformation amount,but the increasing trend becomes slower when the deformation amount is greater than 20%.As the deformation temperature increases,the bonding strength first increases and then decreases,and the bonding strength does not change much when the deformation temperature is 1100℃ and 1250℃.The longer the holding time,the lower the bonding strength of the clad plate is.

关 键 词：复合板 热变形参数 结合强度 

分 类 号：TG142[一般工业技术—材料科学与工程]