玻璃喷墨打印用黑色墨水的制备  

Preparation of Black Ink for Glass Ink Jet Printing

作　　者：刘华锋 刘伟 戴钰 张小珍 陈仁华 Liu Huafeng;Liu Wei;Dai Yu;Zhang Xiaozhen;Chen Renhua(Jiangxi Jinhuan Pigments Co.,Ltd,Yichun 336000,China;School of Materials Science and Engineering,Jingdezhen Ceramic Institute,Jingdezhen 333403,China)

机构地区：[1]江西金环颜料有限公司,宜春336000 [2]景德镇陶瓷大学材料科学与工程学院,景德镇333001

出　　处：《山东陶瓷》2020年第6期1-4,共4页Shandong Ceramics

基　　金：江西省重点研发计划项目(20192BBE50037);江西省重点研发计划项目(20181ACE50017);江西省重点新产品项目(S2019CXCPB0348)。

摘　　要：用液相共沉淀法制备了钼、锌离子同时掺杂铬酸铜黑色颜料,通过扫描电子显微镜观测其原始晶粒尺寸和结晶程度。调制与该色料匹配的环保玻璃熔块,使用温度为690-700℃,将该色料与熔块结合使用,呈现纯正的蓝相黑,同时有良好的遮盖力。再将两者与墨水溶剂、助剂一起磨制玻璃喷墨打印墨水,墨水在玻璃上烧制后,油墨层具有良好的黑度、光泽度、耐酸性、遮盖力。Molybdenum and zinc ions doped copper chromate black pigment was prepared by liquid coprecipitation method.The original grain size and crystallinity were observed by scanning electron microscope.The environmental protection type frit matched with the pigment was prepared and used at 680-700℃.When the frit was used together with the pigment,the pure blue black could be obtained.It has strong covering power at the same time,the glass ink-jet printing ink was prepared by grinding the glass frit and pigment with ink solvent and auxiliary agent.After the ink is fired on glass,the ink layer has good blackness,glossiness,acid resistance and covering power.

关 键 词：铬酸铜 掺杂 环保玻璃熔块 