改善高碱高镁熟料性能的探索与实践  

Exploration and practice of improving the performance of high Alkali and high magnesium clinker

作　　者：朱精瑞 Zhu Jingrui(China Gezhouba Group Cement Co.,Ltd.,Wuhan 430070,China)

机构地区：[1]中国葛洲坝集团水泥有限公司,湖北武汉430070

出　　处：《水泥工程》2021年第2期38-40,共3页Cement Engineering

摘　　要：当阳公司#2线自投产以来,间断性出现熟料需水量高(有时≥140 ml),净浆流动度有时为"零",28 d强度波动大(时常≤53MPa)的情况。配料上通过"钢渣+粉煤灰""、掺入脱硫石膏""、提高硅酸率"等方案;工艺上采用了"强火急冷"思路。降低了原材料波动大、熟料中镁、碱偏高等不利因素,对熟料使用性能的影响。Since Dangyang Line #2 was put into production, the clinker water demand was high(sometimes ≥140 ml), the fluidity of the net slurry was sometimes "zero", and the 28-day strength fluctuation was large(often ≤53 MPa). The ingredients adopted the "steel slag+ fly ash", "mixed with desulfurized gypsum", "increase the rate of silicic acid" and other programs;in the process, the idea of "strong fire and rapid cooling" was adopted. It reduces the unfavorable factors such as large fluctuations of raw materials, high magnesium and alkali in the clinker, which affect the performance of the clinker.

关 键 词：高碱高镁熟料 脱硫石膏使用 熟料性能 高硅酸率 

分 类 号：TQ172.6[化学工程—水泥工业]