7XXX铝合金弹壳外表面残余应力分析  

Analysis on Residual Stress on External Surface of 7XXX Aluminum Alloy Shell Case

作　　者：江长友 金辉 陈露 JIANG Changyou;JIN Hui;CHEN Lu(Chongqing Jialing Special Equipment Co.,Ltd.,Chongqing 400032,China)

机构地区：[1]重庆嘉陵特种装备有限公司,重庆400032

出　　处：《热加工工艺》2021年第12期132-134,142,共4页Hot Working Technology

基　　金：“十三五”国防基础预研项目(41423060312)。

摘　　要：利用X射线衍射法对不同加工状态的7XXX高强度铝合金弹壳的外表面残余应力进行了系统分析。结果表明:不同引长和收口状态的弹壳经退火处理后,能有效减少残余应力;固溶/时效处理后,收口部位和底部的残余应力明显增大,表面残余应力总的表现比未时效的有所提高。The residual stress on the outer surface of 7 XXX high strength aluminum alloy shell case with different processing states was systematically analyzed by X-ray diffraction method. The results show that the residual stress of the shell case with different elongation and closing state can be effectively reduced after annealing. After solid solution/aging treatment,the residual stress at the mouth and bottom increases obviously. The overal performance of surface residual stress is higher than that of without aging.

关 键 词：7XXX铝合金 残余应力 X射线衍射法 弹壳 

分 类 号：TG166.3[金属学及工艺—热处理]