酚脲烷树脂砂在无模复合成形工艺中的应用  

Application of Phenolic Urea Alkanes Resin Sand in Patternless Forming Process

在线阅读下载全文

作  者:邵春艳 杨文亮 孙亮 徐继福 SHAO Chunyan;YANG Wenliang;SUN Liang;XU Jifu(Beijing National Innovation Institute of Lightweight Ltd.,Beijing 100083,China)

机构地区:[1]北京机科国创轻量化科学研究院有限公司,北京100083

出  处:《铸造技术》2021年第6期490-492,共3页Foundry Technology

基  金:国家重点研发计划(2016YFB1101800)。

摘  要:选用106〜212μm水洗砂作为造型材料,酚脲烷树脂为粘结剂,采用自重震实工艺生产砂坯,铣削工艺制备砂型。结果表明,通过调节催化剂种类和加入量改变,砂型的固化时间变化范围在5-60 min,可满足不同节拍的需求;同时树脂加入量为1.5%~2.0%时,砂型的抗拉强度达到1.8〜2.5 MPa以上,符合铣削砂型的工艺要求。Using 106-212μm washed sand as molding material and phenolureane resin as binder,the sand blank was produced by gravity shock compaction process,and the sand mold was prepared by milling process.The results show that by adjusting the type of catalyst and the amount of catalyst,the solidification time of sand mold varies in the range of 5~60 min,which can meet the requirements of different beats.At the same time,when the resin content is 1.5%~2.0%,the tensile strength of sand mold can reach more than 1.8-2.5 MPa,which meets the technological requirements of milling sand mold.

关 键 词:酚脲烷树脂 自重震实工艺 铣削工艺 抗拉强度 

分 类 号:TG242[金属学及工艺—铸造]

 