Influence of phosphorus on iron-based friction material prepared directly vanadium-bearing titanomagnetite concentrates  

作　　者：Yan-yan Zhang Ke-qin Feng Yue Shui Si-tan Chen Yan-fang Liu 

机构地区：[1]School of Mechanical Engineering,Sichuan University,Chengdu 610065,Sichuan,China

出　　处：《Journal of Iron and Steel Research International》2021年第6期669-678,共10页

基　　金：financially supported by the Science and Technology Plan of Panzhihua City in Sichuan Province of China under Grant No.2017CY-C-1.

摘　　要：In situ selective carbothermic reactions and vacuum sintering were used to prepare iron-based friction material directly vanadium-bearing titanomagnetite concentrates.Effects of phosphorus addition(0.05–0.20 wt.%)on the microstructure and properties of iron-based friction material were investigated.The results show that the addition of phosphorus improves the microstructure and properties of the material significantly.When phosphorus addition increases to 0.15 wt.%,the sintering densification is promoted and the number of lamellar pearlites increases.Therefore,the relative density,hardness and tribological properties of the material are greatly enhanced.Particularly,the friction coefficient decreases 0.58 to 0.43,and the wear rate reduces 1.829×10^(–7) to 0.694×10^(–7)cm^(3)J^(-1).The dominant wear mechanism of the material changes severe abrasive wear to mild oxidation wear accordingly.However,when phosphorus addition exceeds 0.15 wt.%,the matrix continuity and tribological properties of the material are deteriorated.Comprehensively,the optimal addition of phosphorus in the iron-based friction material is 0.15 wt.%.

关 键 词：Vanadium-bearing titanomagnetite concentrate Iron-based friction material Tribological behavior PHOSPHORUS 

分 类 号：TF55[冶金工程—钢铁冶金]