Strength and Microstructural Analysis of Geopolymer Prepared with Recycled Geopolymer Powder  

作　　者：WANG Xinjie YANG Wei LIU Hui ZHU Pinghua ZONG Ningwen FENG Jincai 王新杰;YANG Wei;LIU Hui;朱平华;ZONG Ningwen;FENG Jincai(Department of Civil Engineering,Changzhou University,Changzhou,213164,China)

机构地区：[1]Department of Civil Engineering,Changzhou University,Changzhou,213164,China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2021年第3期439-445,共7页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China(No.52008046);the Natural Science Foundation of Jiangsu Higher Education Institutions of China(No.19KJB560007);the Innovation Project of the Jiangsu Postgraduate Research of China(No.KYCX19_1788);the Research Start-up Funding of Changzhou University(No.ZMF18020307)。

摘　　要：The strength and microstructural analysis of recycled geopolymer are presented in this paper.Five kinds of geopolymers containing 0%,20%,50%,80%and 100%of recycled geopolymer powder were prepared using metakaolin as the source material.The alkali activator solution was a mixture of sodium silicate(Na_(2)SiO_(3))and 12 M sodium hydroxide(NaOH).The change laws of compressive and flexural strength of recycled geopolymer specimens were investigated.And the microscopic characteristics were carried out by SEM,XRD and FTIR to observe the internal morphology and analyze changes in components of recycled geopolymers at different substitution rates.The results show that,with the increase of substitution rate of recycled geopolymer powder,the mechanical properties of recycled geopolymers degenerate and the looser structure are formed.When the substitution rate is less than 50%,the recycled geopolymer specimen meets the use requirements of heavy traffic load class.And the specimen with 80%of substitution rate satisfies the requirements of plastering mortar.

关 键 词：recycled geopolymer powder GEOPOLYMER substitution rates mechanical properties MICROSTRUCTURE 