Development of Vertical Buffered Electropolishing for Its Post-Treatment Technology on 1.5GHz Niobium SRF Cavities  

作　　者：JIN Song ATWu LU Xiang-Yang RARimmer LIN Lin ZHAO Kui 靳松;A.T.Wu;鲁向阳;R.A.Rimmer;林林;赵夔(State Key Laboratory of Nuclear Physics and Technology,Institute of Heavy Ion Physics,School of Physics,Peking University,Beijing 100871;Thomas Jefferson National Accelerator Facility,12000 Jefferson Avenue,Newport News,VA 23606,USA)

机构地区：[1]State Key Laboratory of Nuclear Physics and Technology,Institute of Heavy Ion Physics,School of Physics,Peking University,Beijing 100871 [2]Thomas Jefferson National Accelerator Facility,12000 Jefferson Avenue,Newport News,VA 23606,USA

出　　处：《Chinese Physics Letters》2011年第11期91-94,共4页中国物理快报（英文版）

摘　　要：We report the latest research development of vertical buffered electropolishing on its post-treatment procedure as well as the effects of several major post-treatment techniques for buffered electropolishing(BEP)processed 1.5 GHz niobium(Nb)superconducting radio frequency(SRF)cavities.With the established post-treatment procedure,an accelerating gradient of 28.4MV/m is obtained on a single cell cavity of the cebaf shape.This is the best result in the history of BEP development.The cavity is limited by quench with a high quality factor over 1.2×1010 at the quench point.Analyses from optical inspection and temperature-mapping show that the quench should be originated from the pits that were already present on the cavity before this BEP treatment.All of these factors indicate that this procedure will have a great potential to produce better results if cavities without intrinsic performance limiting imperfections are used.

关 键 词：treatment POLISHING cavity 

分 类 号：TG1[金属学及工艺—金属学]