Mechanical Performances of Carbonitriding Films on Cast Iron by Plasma Electrolytic Carbonitriding  

作　　者：PANG Hua ZHANG Gu-Ling WANG Xing-Quan LV Guo-Hua CHEN Huan YANG Si-Ze 庞华;张谷令;王兴权;吕国华;陈睆;杨思泽(Beijing National Laboratory for Condensed Matter Physics,Institute of Physics,Chinese Academy of Sciences,Beijing 100190;Fujian Key Laboratory for Plasma and Magnetic Resonance,Department of Aeronautics,School of Physics and Mechanical and Electrical Engineering,Xiamen University,Xiamen 361005;College of Science,Minzu University of China,Beijing 100081)

机构地区：[1]Beijing National Laboratory for Condensed Matter Physics,Institute of Physics,Chinese Academy of Sciences,Beijing 100190 [2]Fujian Key Laboratory for Plasma and Magnetic Resonance,Department of Aeronautics,School of Physics and Mechanical and Electrical Engineering,Xiamen University,Xiamen 361005 [3]College of Science,Minzu University of China,Beijing 100081

出　　处：《Chinese Physics Letters》2011年第11期243-245,共3页中国物理快报（英文版）

基　　金：by the National Natural Science Foundation of China under Grant Nos 10735090 and 11005151(Young Scientists Fund).

摘　　要：The plasma electrolytic carbonitriding(PEC/N)process is applied to cast iron using an aqueous solution of acetamide and glycerin as the electrolyte.Mechanical properties of the carbonitriding layers on cast iron are investigated.After the PEC/N treatment,the microhardness and wear resistance of cast iron are improved significantly compared to the untreated substrate.When the substrate is processed at 350V for 60 s,the coating presents the highest microhardness and it is about 554.14HK0.02,and the coating with the highest hardness has the best wear resistance.

关 键 词：NITRIDING WEAR COATING 

分 类 号：TG1[金属学及工艺—金属学]