High-temperature deformation behavior and processing map of the as-cast Inconel 625 alloy  

作　　者：Zhi Jia Ze-Xi Gao Jin-Jin Ji De-Xue Liu Ting-Biao Guo Yu-Tian Ding 

机构地区：[1]School of Material Science and Engineering,Lanzhou University of Technology,Lanzhou,730050,China [2]Key State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Lanzhou University of Technology,Lanzhou,730050,China [3]School of Materials Engineering,Lanzhou Institute of Technology,Lanzhou,730050,China

出　　处：《Rare Metals》2021年第8期2083-2091,共9页稀有金属（英文版）

基　　金：financially supported by the National Natural Science Foundation of China(Nos.51665032 and 51664041);the Science Foundation for Distinguished Young Scholars of Gansu Province(No.18JR3RA134)。

摘　　要：A short process of Inconel 625 alloy tube was developed to solve the problems of the traditional extrusion process,and particular attention was paid on the hot deformation behavior of the as-cast Inconel 625 alloy.The hot compression experiments were performed to study the hot deformation behavior of Inconel 625 in the temperature range of 900-1200℃ and strain rate range of0.01-10.00 s^(-1) by Gleeble-3500.The hot compressed microstructure was examined to study the effects of temperature and strain rate on the microstructural characteristic by electron backscatter diffraction(EBSD).The results show that the processing maps were greatly influenced by the temperature rather than the strain rate.It is found that with the strain increasing,the instability zone gradually turned to the low-temperature and low strain rate area,while the range of high-temperature instability area shrank.The optimum condition of the as-cast Inconel 625 alloy was determined as high strain rate region(temperature of1100-1200℃,strain rate of 1.00-10.00 s^(-1))with the dissipation efficiency of above 0.28.As illustrated by microstructural characteristic of EBSD analysis,the perfect dynamic recrystallization occurred and fine grain structure was obtained under this deformation conditions.

关 键 词：Inconel 625 Hot deformation behavior Constitutive equation MICROSTRUCTURE Processing map 