高含量碳纤维三维织物的织造技术探究  

Study on weaving technology of 3D woven fabrics withhigh content carbon fibers

作　　者：谭冬宜[1] 汪泽幸[1] 王坤[1] 何斌[1] Tan Dongyi;Wang Zexing;Wang Kun;He Bing(College of Textile and Fashion,Hunan Institute of Engineering,Xiangtan 411104,China)

机构地区：[1]湖南工程学院纺织服装学院,湖南湘潭411104

出　　处：《产业用纺织品》2021年第7期48-50,共3页Technical Textiles

基　　金：国家级大学生创新创业训练计划项目(201711342003);湖南省自然科学基金项目(2016JJ6030);湖南省教育厅优秀青年项目(16B059)。

摘　　要：以双酚A型水性环氧树脂为主浆料,对经纬纱用碳纤维复丝进行上浆处理,并设计和试织了7层层间正交碳纤维三维机织物,并与未经上浆处理试织的织物对比。结果发现:上浆处理能增加碳纤维单丝间的抱合力,改善经纱表面起毛及纬纱折幅时易脆断的状况,所织制的碳纤维三维织物表面比较光洁。Using bisphenol A waterborne epoxy resin as the main sizing material,the carbon multifilament for warp and weft yarns were sized,and the carbon fiber 3D woven fabric with orthogonal structure between seven layers was designed and tested.The results show that,sizing treatment can increase the binding force between the carbon monofilaments,improve the warp surface fuzz and weft folding brittle condition.The surface of the carbon fiber 3D woven fabric is relatively smooth.

关 键 词：碳纤维 三维织物 上浆 层间正交结构 

分 类 号：TS106.6[轻工技术与工程—纺织工程]