白炭黑胎面胶配方中促进剂DPG的替代试验研究  

Experimental Study on Substitution of Accelerator DPG in Silica Tread Compound Formula

作　　者：刘震 王小菊 于晓波 LIU Zhen;WANG Xiaoju;YU Xiaobo(EVE Rubber Institute Co.,Ltd,Qingdao 266045,China;Qingdao Key Laboratory of Tire New Materials,Qingdao 266045,China)

机构地区：[1]怡维怡橡胶研究院有限公司,山东青岛266045 [2]青岛市轮胎新材料重点实验室,山东青岛266045

出　　处：《橡胶科技》2021年第9期436-440,共5页Rubber Science and Technology

摘　　要：研究在典型的白炭黑胎面胶配方中用促进剂DPT和TATD替代促进剂DPG的应用效果。结果表明:虽然促进剂DPG高温裂解会产生危害人体健康和环境的苯胺,但其在白炭黑胎面胶配方中的综合性能优势比较明显;促进剂DPT替代促进剂DPG在硫化体系上需要进行适当调整,同时要注意其对胶料门尼粘度、拉伸强度及拉断伸长率等的影响;促进剂TATD替代促进剂DPG的难度较大,替代后混炼胶的加工性能和硫化胶的物理性能都发生了比较明显的变化;在白炭黑胎面胶配方中促进剂DPG替代不能进行简单的品种更换,同时需对配方其他组分进行优化调整。The application effect of accelerator DPT and TATD as the substitute of the accelerator DPG in a typical silica tread compound formula was studied.The results showed that,despite the high temperature cracking of accelerator DPG could produce aniline,which was harmful to human health and the environment,its comprehensive performance advantage in the formula of silica tread compound was obvious.When the accelerator DPT was used to replace accelerator DPG,the vulcanization system should be properly adjusted,and its effects on the Mooney viscosity,tensile strength and elongation at break of the compound should be paid attention to.However,it was difficult for the accelerator TATD to simply replace accelerator DPG in the compound.It was found that after the replacement,the processing properties of the compound and the physical properties of the vulcanizate had undergone obvious changes.In the formula of the silica tread compound,the accelerator DPG could not be replaced by simple accelerator change,and other components of the formula needed to be optimized and adjusted.

关 键 词：促进剂 白炭黑胎面胶 替代 PAYNE效应 动态力学性能 环保 

分 类 号：TQ336.1[化学工程—橡胶工业] TQ330.385