电磁场对3003铝合金铸轧板材组织的影响  

Effect of electromagnetic field on microstructure of 3003 aluminum alloy cast-rolling sheet

作　　者：吕野楠[1,2] 丁韧 许光明[1] 尤涛 Lü Ye-nan;DING Ren;XU Guang-ming;YOU Tao(Mechatronic Department,Liaoning Provincial College of Communications,Shenyang 110122,China;Key Laboratory of Electromagnetic Processing of Materials,Ministry of Education,Northeastern University,Shenyang 110819,China)

机构地区：[1]辽宁省交通高等专科学校机电系,辽宁沈阳110122 [2]东北大学材料电磁过程研究教育部重点实验室,辽宁沈阳110819

出　　处：《轻合金加工技术》2021年第9期11-14,共4页Light Alloy Fabrication Technology

基　　金：辽宁省自然科学基金项目(2019-ZD-0314);辽宁省教育厅科研项目(12019637)。

摘　　要：在传统铸轧过程中施加电磁场生产3003铝合金板材,对比分析传统铸轧板材与施加电磁场条件下铸乳板材的显微组织。结果表明:在铸轧过程中施加电磁场可以有效地改善显微组织,破碎枝晶、细化晶粒;电磁场能抑制自然对流,加速溶质扩散,减少偏析;同时发现,电磁场使铁相粒子聚集,在铸轧板材一定区域形成宏观偏析带。Traditional roll-casting test and electromagnetic field roll-casting test for 3003 aluminum alloy were performed.Microstructures of cast-rolling sheets obtained under the two conditions were contrasted and analysed.The results show that applying electromagnetic field during casting and rolling can improve microstructure,restrain the broken coarse dendrite and refine grains.It can restrain the natural convection,enhance the solute diffusion,and reduce the dendrite segregation.It's also found that electromagnetic field can make iron particles agglomerate,and the macro-segregation band appears in a certain area of the cast-rolling sheet.

关 键 词：3003铝合金 铸轧 电磁场 显微组织 偏析 