Fe-Cr-Al合金氧化膜的形貌表征及性能  

Morphology Characterization and Properties of Oxide Film for Fe-Cr-Al Alloy

作　　者：华脂亭 韩丽平 吕晓霞[1] HUA Zhi-ting;HAN Li-ping;Lü Xiao-xia(School of Materials Science and Engineering,Jilin University,Changchun 130022,Jilin,China)

机构地区：[1]吉林大学材料科学与工程学院,吉林长春130022

出　　处：《铸造》2021年第9期1068-1071,共4页Foundry

基　　金：吉林大学“大学生创新创业训练计划”项目(2018B1615);吉林大学“大学生开放性创新实验”项目(436OEP74)。

摘　　要：利用高温氧化处理Fe-24Cr-4Al合金表面,制备了Fe-24Cr-4Al合金表面氧化膜。并采用X射线衍射仪、光学金相显微镜、扫描电镜及能谱检测等多种组织与形貌表征手段,对Fe24Cr-4Al合金表面氧化层进行了显微组织的表征以及显微硬度的测定。结果表明:Fe-24Cr4Al合金最佳氧化温度为1250℃,此温度下可得到平整性和致密度较好的氧化膜,且氧化膜具有较高的硬度。The surface oxide film of Fe-24Cr-4Al alloy was prepared by high temperature oxidation treatment.By means of X-ray diffraction,optical metallographic microscope,scanning electron microscope and energy spectrum analysis,the microstructure and hardness of the oxide layer on the surface of Fe-24Cr-4Al alloy were characterized.The results show that the optimal oxidation temperature of Fe-24Cr-4Al alloy is 1250℃.At this temperature,a smooth and dense oxide film can be obtained,and the film has a high hardness.

关 键 词：高温氧化 Al_(2)O_(3) 微观形貌 硬度 FE-CR-AL合金 

分 类 号：TG132.24[一般工业技术—材料科学与工程]