Corrosion resistance of Ca-P coating induced by layer-by-layer assembled polyvinylpyrrolidone/DNA multilayer on magnesium AZ31 alloy  

作　　者：Zhen-Yu ZHANG Duo WANG Lu-Xian LIANG Shen-Cong CHENG Lan-Yue CUI Shuo-Qi LI Zhen-Lin WANG Rong-Chang ZENG 

机构地区：[1]College of Materials Science and Engineering,Shandong University of Science and Technology,Qingdao 266590,China [2]School of Materials Science and Engineering,Zhengzhou University,Zhengzhou 450002,China [3]College of Materials Science and Engineering,Chongqing University of Technology,Chongqing 400065,China

出　　处：《Frontiers of Materials Science》2021年第3期391-405,共15页材料学前沿（英文版）

基　　金：This work was supported by the National Natural Science Foundation of China(Grant No.52071191);the Natural Science Foundation of Shandong Province(ZR2020QE009);the Research Start-up Fund of Shandong University of Science and Technology(01040125219);the“Elite Plan”Foundation of Shandong University of Science and Technology(0104060541112).

摘　　要：A hydrothermal deposition method was utilized to fabricate Ca-P composite coating induced by the layer-by-layer(LbL)assembled polyvinylpyrrolidone/deoxyribonucleic acid(PVP/DNA)_(20) multilayer on AZ31 alloy.The surface morphology and compositions were characterized by SEM,EDS,FTIR and XRD.Besides,the corrosion resistance and degradation behavior of the coating were tested via electrochemical polarization,impedance spectroscopy and immersion measurements.Results show that the main components of Ca-P coatings are hydroxyapatite,Ca_(3)(PO_(4))_(2) and Mg_(3)(PO_(4))_(2)·nH_(2)O.The LbL-assembled DNA and PVP promote the adsorption of Ca-P deposits on the sample surface,and structures and functional groups of the polyelectrolyte in the outermost layer are the primary influencing factor for the induction of the Ca-P coating.Carboxyl groups have the best biomineralization effect among all related functional groups.The enhanced corrosion resistance and adhesion highlight a promising use of(PVP/DNA)_(20)-induced Ca-P coatings in the field of biomedical magnesium alloys.

关 键 词：magnesium alloy biomaterial corrosion layer-by-layer assembly Ca-P coating 

分 类 号：TG174.4[金属学及工艺—金属表面处理]