高性能环氧厚浆云铁中间漆的制备  

Preparation of High-performance Epoxy-thick Slurry Cloud-iron Intermediate Paint

作　　者：王雷 李华明 雍涛 苏岳雄 靳生红 卜万保 WANG Lei;LI Hua-ming;YONG Tao;SU Yue-xiong;JI Sheng-hong;BU Wan-bao(Northwest Yongxin Paints&Coatings Co.,Ltd.,Lanzhou 730046,China;Gansu Traffic Construction Project Management Co.,Ltd.,Lanzhou 730030,China)

机构地区：[1]西北永新涂料有限公司,兰州730046 [2]甘肃交建项目管理有限公司,兰州730030

出　　处：《现代涂料与涂装》2021年第10期1-4,共4页Modern Paint & Finishing

摘　　要：环氧云铁中间漆通常作为防腐配套涂层的中间层,不仅起到增加涂层厚度的作用,还具有优异的耐酸碱、耐化学品性能。木文主要论述了环氧厚浆云铁中间漆的制备方法,其漆膜可在低温下固化,且具有优异的耐酸碱和耐化学品性能;体积固含为80%,挥发性有机溶剂含量少,一遍施工厚度可达150μm以上,符合环境友好型涂料的发展方向。Epoxy iron-cloud paint is used as the intermediate layer of anticorrosion supporting coating.It not only plays the role of increasing the thickness of coating,but also requires that the coating has excellent acid and alkali resistance and chemical resistance.The preparation method of epoxy-thick slurry iron-cloud intermediate paint was discussed.The film can be cured at low temperature,and has excellent acid and alkali resistance and chemical resistance.The volume solid content is 80%,the content of volatile organic solvents is less,the thickness of one construction can reach more than 150μm,in line with the development direction of environment-friendly coating.

关 键 词：环氧云铁中间漆 耐酸碱性能 低温固化 挥发性有机溶剂 

分 类 号：TQ633[化学工程—精细化工]