优化进口矿粉与钒钛精粉比例提高烧结矿冶金性能的研究  

Study on optimizing the ratio of imported ore powder and vanadium-titanium powder to improve the metallurgical properties of sinter

作　　者：秦洋洋 王涛 刘正勇 张明远[1] QIN Yangyang;WANG Tao;LIU Zhengyong;ZHANG Mingyuan(School of Metallurgy and Materials Engineering,Chongqing University of Science and Technology,Chongqing 401331,China)

机构地区：[1]重庆科技学院冶金与材料工程学院,重庆401331

出　　处：《四川冶金》2021年第5期4-8,共5页Sichuan Metallurgy

基　　金：国家自然科学基金项目(51604054)。

摘　　要：针对威钢现有烧结配料系统中钒钛精粉配比较低的问题,进行了烧结杯实验,并对实验所得烧结矿进行冶金性能检测及研究。结果表明:在钒钛精粉配比10%~40%的范围内,随着钒钛精粉配比的增加,烧结矿低温还原粉化率降低;还原度先下降后小幅上升;软化开始温度升高,滴落温度降低,软融区间变窄;成品率、转鼓指数、抗磨指数均降低。从目前威钢生产条件来看,钒钛精粉配比为30%时为宜。在此条件下,烧结矿的抗磨指数为5.97%,转鼓指数为66.67%,达到烧结矿冷强度国家标准;其还原性(RI)为81.62%、低温还原粉化率(RDI+3.15)为41.92%和软熔区间为128℃,符合入炉标准。本结果可为钒钛矿烧结合理配矿提供指导。Aiming at the problem that Weigang's existing sintering batching system is relatively low in the proportion of vanadium-titanium refined powder,a sinter cup experiment was carried out,and the metallurgical properties of the sinter obtained from the experiment were tested and studied.The results show that:in the range of 10%-40%of the vanadium-titanium concentrate ratio,with the increase of the vanadium-titanium concentrate ratio,the low-temperature reduction pulverization rate of the sinter decreases;the degree of reduction first decreases and then rises slightly;the softening start temperature As it increases,the dripping temperature decreases,and the soft-melting interval narrows;the yield,drum index,and anti-wear index all decrease.Judging from the current production conditions of Weigang,it is appropriate when the ratio of vanadium-titanium concentrate is 30%.Under these conditions,the abrasion resistance index of the sinter is 5.97%,and the drum index is 66.67%,which meets the national standard for cold strength of the sinter;its reducibility(RI)is 81.62%,and the low-temperature reduction pulverization rate(RDI+3.15)It is 41.92%and the reflow interval is 128℃,which meets the furnace entry standard.The results can provide guidance for the rational blending of vanadium-titanium ore sintering.

关 键 词：烧结 钒钛矿 优化配矿 冶金性能 

分 类 号：TF046.4[冶金工程—冶金物理化学]