基于HyperXtrude的大宽厚比工业铝型材挤压速度优化  

Extrusion speed optimization on industrial aluminum profiles with large width to thickness ratio based on HyperXtrude

作　　者：张德军[1] 林春梅[1] 孙巧妍[1] 党军建[1] 曲庆文 吕正风 Zhang Dejun;Lin Chunmei;Sun Qiaoyan;Dang Junjian;Qu Qingwen;Lyu Zhengfeng(Mechanical Department,College of Engineering Yantai Nanshan University,Yantai 265713,China;Shandong Nanshan Aluminum Co.,Ltd.,Longkou 265713,China)

机构地区：[1]烟台南山学院工学院机械系,山东烟台265713 [2]山东南山铝业股份有限公司,山东龙口265713

出　　处：《锻压技术》2021年第10期156-160,共5页Forging & Stamping Technology

基　　金：山东省重大科技创新工程项目(2018CXGC0401);山东省自然科学基金资助项目(ZR2017PEM005);山东省重点研发计划(软科学项目)(2019RKA06034)。

摘　　要：为了优化大宽厚比工业铝型材的挤压速度,以某大宽厚比空心6005A工业铝材为例,利用HyperXtrude软件,针对不同的挤压速度进行了稳态挤压数值模拟仿真。结果表明:当挤压速度大于2.2 mm·s^(-1)时,型材的出口速度和出口温度不均匀性随着挤压速度的增大而迅速增加;当挤压速度大于3.4 mm·s^(-1)时,挤压力会超出挤压机的最大极限压力。最后,利用挤压生产理论知识对仿真结果进行对比分析,确定了该大宽厚比6005A空心铝合金型材在90 MN挤压机上的合理挤压速度范围为1.0~2.2 mm·s^(-1)。利用优化后的挤压速度进行实际生产,挤压出合格的型材,证明了挤压速度优化数值的可靠性。In order to optimize the extrusion speed of industrial aluminum profiles with large width to thickness ratio,for a certain hollow industrial 6005 A aluminum profile with large width to thickness ratio,and the numerical simulation of steady-state extrusion for different extrusion speeds was conducted by software HyperXtrude.The results show that when the extrusion speed is greater than 2.2 mm·s^(-1),the inhomogeneities of outlet speed and outlet temperature increase rapidly with the increasing of extrusion speed.When the extrusion speed is greater than 3.4 mm·s^(-1),the extrusion pressure exceeds the maximum ultimate pressure of extruder.Finally,using the theoretical knowledge of extrusion production to compare and analyze the simulation results,it is determined that the reasonable extrusion speed range of the hollow 6005 A aluminum alloy profile with large width to thickness ratio on the extruder of 90 MN is 1.0-2.2 mm·s^(-1).The optimized extrusion speed is used for the actual production,and the qualified profiles are extruded to prove the reliability of the optimized values of extrusion speed.

关 键 词：大宽厚比铝型材 铝材挤压 HYPERXTRUDE 挤压速度 

分 类 号：TG146.21[一般工业技术—材料科学与工程]