高结构炭黑NC8515在全钢子午线轮胎胎面胶中的应用  

Application of High Structure Carbon Black NC8515 in Tread Compound of All-steel Radial Tire

作　　者：陈新中 柳云点 丁利虎 刘明燕 孙鲁光 唐俊萍 CHEN Xinzhong;LIU Yundian;DING Lihu;LIU Mingyan;SUN Luguang;TANG Junping(Shandong NAIST Carbon Black Co.,Ltd,Dongying 257506,China;Shandong Wanda Boto Tyre Co.,Ltd,Dongying 257506,China)

机构地区：[1]山东耐斯特炭黑有限公司,山东东营257506 [2]山东万达宝通轮胎有限公司,山东东营257506

出　　处：《橡胶科技》2021年第11期540-543,共4页Rubber Science and Technology

摘　　要：研究高结构炭黑NC8515在全钢子午线轮胎胎面胶中的应用。结果表明:炭黑NC8515的氮吸附比表面积和外表面积均较炭黑N234小,但吸油值和压缩样吸油值大于炭黑N234,结构高;炭黑NC8515的粒径略大于炭黑N234,但其聚集体及粒径分布无明显差别;添加炭黑NC8515的混炼胶的门尼焦烧时间延长,加工安全性提高,硫化胶的生热和滚动阻力降低,耐磨性能提高;成品轮胎路试结果差异不大,单位磨耗行驶里程为22600~24000 km。The application of high structure carbon black NC8515 in the tread compound of all-steel radial tire was studied.The results showed that,the nitrogen adsorption specific surface area and external surface area of carbon black NC8515 were smaller than those of carbon black N234,but the oil absorption value and compressed oil absorption value were higher.The particle size of carbon black NC8515 was slightly larger than that of carbon black N234,but there was no significant difference in aggregate and particle size distribution.The Mooney scorch time of the compound with carbon black NC8515 was prolonged,the processing safety was improved,the heat build-up and rolling resistance of the vulcanizate were reduced and the wear resistance was improved.The road test results of the finished tire with carbon black NC8515 filled tread compound had little difference from the tire with carbon black N234,and the driving mileage per unit wear was between 22600~24000 km.

关 键 词：全钢子午线轮胎 胎面胶 高结构炭黑 粒径分布 耐磨性能 生热 

分 类 号：TQ330.[化学工程—橡胶工业]