红柱石在烧结刚玉基窑口浇注料中的应用  

Application of Andalusite in sintering corundum based castable for kiln mouth

作　　者：张彦 Zhang Yan(Jiangsu Tianshan Group Cement Co.,Ltd.,Wuxi,214255,China)

机构地区：[1]江苏天山集团水泥有限公司,江苏无锡214255

出　　处：《水泥工程》2021年第5期33-35,共3页Cement Engineering

摘　　要：以烧结刚玉、碳化硅等为主要原料,分别以红柱石0%、5%、10%、15%替换相同比例的烧结刚玉,同时外加少量的改性剂A制备四组浇注料,对比四种浇注料经1 400℃处理后的常温性能、线变化、抗热震性、抗碱侵蚀能力。结果表明,添加红柱石10%和改性剂1%的烧结刚玉基窑口浇注料表现出较好的使用性能。Four groups of castables were prepared by using sintered corundum and silicon carbide as main raw materials, respectively replacing sintered corundum with 0%, 5%, 10% and 15% andalusite, and adding a small amount of modifier A. The room temperature performance, linear change, thermal shock resistance and alkali corrosion resistance of the four castables after 1 400 ℃ treatment were compared. The results show that the castable with 10% andalusite and 1% modifier has good performance.

关 键 词：窑口浇注料 红柱石 改性剂 强度 抗热震性 抗碱性 