轨道车辆不锈钢车体激光焊部分熔透搭接接头焊接痕迹研究  

Research on weld mark of laser beam welding partial penetration lap joint for railway vehicle stainless steel carbody

作　　者：邬瑞峰 王秀义 曹思农 安吉 高昆 WU Rui-feng;WANG Xiu-yi;CAO Si-nong;AN Ji;GAO Kun(CRRC Tangshan Co.,Ltd.,Tangshan 063035,Hebei pro.,China;Tianjin CRRC Tangshan Co.,Ltd.,Tianjin 300300,China)

机构地区：[1]中车唐山机车车辆有限公司,河北唐山063035 [2]天津中车唐车轨道车辆有限公司,天津300300

出　　处：《焊接技术》2021年第11期31-34,I0011,共5页Welding Technology

摘　　要：根据部分熔透搭接激光焊工艺特点和结合不锈钢车体侧墙结构,采用不同规格厚度及表面加工类型组合及不同激光焊工艺进行试件焊接,焊后目视检测焊接痕迹的可接受性。试验结果表明:下板至少需选择2.0 mm及以上厚度,焊接方向与拉丝方向相同时焊接后未焊接侧外观质量最好;下板熔深s在0.3~0.6 mm时,厚2.0 mm下板未焊接侧外观美观质量均可以达到要求。从外观美观要求出发,采用连续焊接方式,下板未焊接侧外观质量更优。According to the characteristics of laser beam welding partial penetration lap process and the structure of side wall of stainless steel carbody, different dimensions and thickness, combination of surface processing types and different laser beam welding processes were used to weld specimens. After being welded, visual inspection was conducted to observe the acceptability of weld mark. The test results showed that the thickness of the bottom plate should be at least 2.0 mm or above, and the appearance quality of the unwelded side of the bottom plate was the best when the welding direction was the same as the drawing direction. When the bottom plate penetration depth s was0.3~0.6 mm, the appearance quality of unwelded side of 2.0 mm bottom plate could meet the requirements. From the perspective of requirements of good appearance quality, by using the continuous welding method, the appearance quality of the unwelded side of the bottom plate was better.

关 键 词：激光焊 部分熔透搭接接头 焊接痕迹 

分 类 号：TG456.7[金属学及工艺—焊接]