The effect of powder size on the mechanical and corrosion properties and the ignition temperature of WE43 alloy prepared by spark plasma sintering  

作　　者：Drahomír Dvorský JiríKubásek Michaela Roudnická Filip Pruša David Necas Peter Minárik Jitka Stráská Dalibor Vojtech 

机构地区：[1]University of Chemistry and Technology,Faculty of Chemical Technology,Department of Metals and Corrosion Engineering,Technická516628 Praha 6–Dejvice,Prague,Czech Republic [2]Institute of Physics,Czech Academy of Science,Na Slovance 1999/218221 Praha 8,Prague,Czech Republic [3]Department of Physics of Materials,Charles University,Ke Karlovu 5,Prague 12116,Czech Republic

出　　处：《Journal of Magnesium and Alloys》2021年第4期1356-1369,共14页镁合金学报（英文）

基　　金：The authors wish to thank the Czech Science Foundation(Project No.GA19-08937S);specific university research(A2_FCHT_2020_027 and A1_FCHT_2020_003)for the financial support of this research.

摘　　要：Powder metallurgy is a powerful method for the preparation of materials with superior properties.This work aimed to investigate the effect of powder size on the microstructure,mechanical,and corrosion properties of advanced WE43(Mg-4Y-3REE-Zr)alloy prepared by spark plasma sintering(SPS).At the same time,the effect of HF pre-treatment of the powder on the properties of final compacted products is studied.Smaller powder particles yielded microstructure with more interfaces formed by Y_(2)O_(3),or MgF_(2) and YF_(3).These interfaces work as barriers against corrosion,which greatly improves corrosion resistance.The suggested pre-treatment of powder in HF further reduced the corrosion rate of the compacted materials.On the contrary,fragile interfaces of YF_(3) decreased mechanical properties as the crack primarily propagates through these interfaces.The original powder containing the mixture of all powder fractions exerted the best combination of mechanical properties.Powder size has also shown to affect ignition temperature.The highest ignition temperature was measured for the finest powder fraction.

关 键 词：Powder metallurgy Mechanical properties Corrosion Interface SPS 

分 类 号：TG146.22[一般工业技术—材料科学与工程]