中空笼状多孔结构镍钴层状氢氧化物的制备及其电化学性能  

Fabrication and electrochemical properties of hollow cage-like nickel cobalt layered hydroxides with porous structure

作　　者：杨文 丁倩瑶[1] 翟冬梅 薄开雯 冯艳艳 文婕 何方[1,2] Yang Wen;Ding Qian-Yao;Zhai Dong-Mei;Bo Kai-Wen;Feng Yan-Yan;Wen Jie;He Fang(Guangxi Key Laboratory of Electrochemical and Magneto-chemical Functional Materials,College of Chemistry and Bioengineering,Guilin University of Technology,Guilin 541004,China;College of Chemistry and Bioengineering,Guilin University of Technology,Guilin 541004,China;College of Chemistry and Chemical Engineering,Southwest Petroleum University,Chengdu 610500,China)

机构地区：[1]桂林理工大学化学与生物工程学院,广西电磁化学功能物质重点实验室,桂林541004 [2]桂林理工大学化学与生物工程学院,桂林541004 [3]西南石油大学化学化工学院,成都610500

出　　处：《物理学报》2022年第1期293-302,共10页Acta Physica Sinica

基　　金：广西自然科学基金(批准号:2017GXNSFBA198124,2017GXNSFBA198193);国家自然科学基金(批准号:21606058);广西电磁化学功能物质重点实验室基金(批准号:EMFM20211101)资助的课题。

摘　　要：超级电容器以功率密度高、寿命长、环境友好等优点在各种能量存储设备中受到广泛关注.所以,提高电极材料的储能性能对超级电容器的开发与应用具有重要的意义.具有特定纳米结构的功能材料作为超级电容器电极材料时具有优异的电化学性能,原因在于其能提供丰富的电化学活性位点、高的比表面积和增加电解质与材料的接触面积.因此,本文以ZIF-67纳米晶为模板,利用硝酸盐刻蚀的方法制备中空笼状镍钴层状氢氧化物(NiCo-LDH),并研究其作为超级电容器电极材料的储能性能.借助X射线衍射、扫描电镜、透射电镜、低温氮气吸附/脱附和电化学测试等手段分析所得NiCo-LDH的结构、形貌和电化学性能.结果表明:NiCo-LDH由纳米片组装形成中空笼状结构,拥有丰富的介孔和大孔孔道以及较高的比表面积,从而有助于增加电活性位点,促使电解液与电极材料的充分接触,进而显著提高材料的储能性能.当刻蚀用镍、钴盐质量比为1∶1时,样品Ni_(1)Co_(1)-LDH的比电容可达801 F·g^(-1)(电流密度为0.5 A·g^(-1)),且在大电流密度下(10 A·g^(-1))仍能保持582 F·g^(-1)的比电容;在电流密度15 A·g^(-1)的条件下经过2000次循环后,其比电容值保持为初始值的100.2%,表现出优异的储能性能和潜在的应用价值.Supercapacitors have attracted extensive attention in various storage devices due to their high power density,long life and friendly environment.Hence,improving the energy storage performances of electrode materials are of great significance for supercapacitors.Functional materials with specific nanostructures,as energy storage materials,can display excellent electrochemical performances,for they will provide rich electrochemically active sites,high specific surface area and enhance electrolyte contact area.Consequently,hollow cage-like nickel cobalt layered hydroxides(NiCo-LDH)are prepared via nitrate etching of ZIF-67 nanocrystals,and investigated as electrode materials of supercapacitor.The morphology,structure and electrochemical properties of the obtained materials are investigated by X-ray diffraction,scanning electron microscope,transmission electron microscope,N_(2) adsorption/desorption and a series of electrochemical tests(including cyclic voltammetry,galvanostatic charge and discharge and AC impedance).The results show that the NiCo-LDH samples assembled by nanosheets present a porous structure with hollow cages and high specific area surfaces,which conduces to increasing the electroactive sites,enhancing the contact between the electrolyte and the electrode material,and thus significantly improving the electrochemical performance of the materials.With the mass ratio of nickel to cobalt salt being 1∶1,the specific capacitance of Ni1Co1-LDH is 801 F·g^(-1) at a current density of 0.5 A·g^(-1),and a specific capacitance of 582 F·g^(-1) can still be maintained at a high current density of 10 A·g^(-1).Moreover,the specific capacitance retention of Ni_(1)Co_(1)-LDH is 100.2%after 2000 cycles at a current density of 15 A·g^(-1),displaying good electrochemical performance and great potential in supercapacitor applications.

关 键 词：ZIF-67 镍钴双金属氢氧化物 多孔结构 中空笼状 

分 类 号：TM53[电气工程—电器] O611.64[理学—无机化学]