生物质纤维/菠萝叶纤维多组分混纺纱线的品质与性能  

Quality and performance of biomass fiber/pineapple leaf fiber multi-component blended yarn

作　　者：闵小豹 潘志娟[1,2] MIN Xiaobao;PAN Zhijuan(College of Textile and Clothing Engineering, Soochow University, Suzhou, Jiangsu 215021, China;National Engineering Laboratory for Modern Silk(Suzhou), Suzhou, Jiangsu 215123, China)

机构地区：[1]苏州大学纺织与服装工程学院,江苏苏州215021 [2]现代丝绸国家工程实验室(苏州),江苏苏州215123

出　　处：《纺织学报》2022年第1期74-79,共6页Journal of Textile Research

摘　　要：菠萝叶纤维粗且长,表面有枝节,纵向平直,单独成纱质量较差,为提高其可纺性,结合绢丝、羊毛、壳聚糖纤维、Lyocell纤维和聚乳酸(PLA)纤维的性能特点,选取绢纺系统将菠萝叶纤维分别与这几种纤维混纺制备16.7 tex×2两组分纱线和14.3 tex×2三组分纱线,并测试其力学性能、条干均匀度、毛羽等指标。结果表明:所纺纱线断裂强度高、条干均匀度好、毛羽少,可用于开发中高档机织面料并应用于服装领域;两组分混纺纱中菠萝叶纤维/绢丝(质量比为85∶15)性能较好,断裂强度为(21.9±2.3)cN/tex,毛羽值为3.61 mm/cm,条干CV值为18.05%;三组分混纺纱中菠萝叶纤维/绢丝/Lyocell纤维(质量比为50∶30∶20)性能最优,断裂强度为(19.9±1.3)cN/tex,毛羽值为3.26 mm/cm,条干CV值为14.03%。Pineapple leaf fibers are thick,long,straight,and with branches on the surface,leading to poor quality of pure spun yarn.In order to improve its spinnability,the silk spinning system was employed to blend pineapple leaf fiber with some biomass fibers to prepare 16.7 tex×2 two-component yarns and 14.3 tex×2 three-component yarns,the selected biomass fibers including spun silk,wool,chitosan fiber,Lyocell fiber and polylactic acid(PLA)fiber.The mechanical properties,evenness and hairiness of the yarns were evaluated,and the results show that the spun yarns have high breaking strength,good evenness and low hairiness,which can be used to develop medium to high grade woven fabrics and can be applied to clothing making.Among the two-component blended yarns,the performance of pineapple leaf fiber/spun silk(mass ratio:85∶15)is the best,with breaking strength being(21.9±2.3)cN/tex,the hairiness value 3.61 mm/cm,and the evenness CV value 18.05%.Among the three-component blended yarns,the performance of pineapple leaf fiber/spun silk/Lyocell fiber(mass ratio:50∶30∶20)is the best,whose breaking strength is(19.9±1.3)cN/tex,the hairiness value 3.26 mm/cm,and the evenness CV value 14.03%.

关 键 词：菠萝叶纤维 绢纺系统 多组分混纺纱 力学性能 条干均匀度 毛羽 

分 类 号：TS106.5[轻工技术与工程—纺织工程]