异丙醇铝水解制高纯拟薄水铝石  

Preparation of high purity pseudo-boehmite by hydrolysis of aluminium isopropanol

作　　者：田朋[1] 李伟[1] 杨雨哲 刘坤吉 徐前进 宁桂玲[1] TIAN Peng;LI Wei;YANG Yuzhe;LIU Kunji;XU Qianjin;NING Guiling(Dalian University of Technology-Baohong Technology United Research Center for Advanced Lithium Battery Materials,Chemical Engineering Institute of Dalian University of Technology,Dalian 116023,China;Jiangxi Baohong Nanotechnology Co.,Ltd.)

机构地区：[1]大连理工大学-宝弘科技锂电新材料联合研究中心,大连理工大学化工学院,辽宁大连116023 [2]江西宝弘纳米科技有限公司

出　　处：《无机盐工业》2022年第2期54-59,共6页Inorganic Chemicals Industry

基　　金：大连市高层次人才创新支持计划(青年科技之星),多孔高纯氧化铝清洁制备技术,2018R15。

摘　　要：采用异丙醇铝水解制备拟薄水铝石,考察用水量[n(水)∶n(异丙醇)为2∶1~4.5∶1]、水解时间(0~3 h)、干燥温度(75~120℃)、干燥时间(2~10 h)对拟薄水铝石碳含量、晶相、胶溶指数和水化效果的影响。结果表明,制备条件的改变都会影响产物的碳含量,其中用水量影响最为明显。用水量不断增大,产物的结晶度提高,胶溶指数由2.3%增大到95%以上;延长水解时间有利于产物晶粒的生长和胶溶指数的提高(由35.4%增大到65%以上);干燥温度和干燥时间对产物的晶型和胶溶指数影响较小。此外,产物水化后胶溶指数均大幅度提高,水解过程用水量[n(水)∶n(异丙醇)]大于3∶1时,水化后胶溶指数均能达到99%以上,为异丙醇铝水解制备拟薄水铝石的工业化提供相应的研究基础。Pseudo-boehmite was prepared by hydrolysis of aluminium isopropoxide.The effect of water dosages(the molar ratio of water to aluminum isopropanol was 2∶1~4.5∶1),hydrolysis time(0~3h),drying temperature(75~120℃) and drying time(2~10h) on the residual carbon content,crystal phase,dispersion index and hydration effect were investigated.The results showed that the changes of preparation conditions all affected the carbon content of the product,and the effect of water dosage was the most obvious.With the increase of water dosage,the crystal form of the product was continuously improved,and the dispersion index increased from 2.3% to more than 95%.Prolonging the hydrolysis time was beneficial to the grain growth of pseudo-boehmite and the increase of dispersion index(from 35.4% to more than 65%).Drying temperature and drying time had little effect on the crystal form and dispersion index of pseudo-boehmite.In addition,after the hydration of the obtained products,the dispersion index of the products had been greatly improved.When the ratio of water to aluminum isopropanol in the hydrolysis process was more than 3∶1,the dispersion index could reach more than 99% after hydration,which provided a research basis for the industrialization of the preparation of pseudo-boehmite by the hydrolysis of aluminium isopropoxide.

关 键 词：异丙醇铝 高纯拟薄水铝石 碳含量 胶溶指数 水化 