溶胶-凝胶法制备有机玻璃镀膜板表面高透光率耐磨涂层  

Preparation of High Light Transmittance and Wear-resistant Coating on the Surface of PMMA Coated Plate by Sol-gel Method

作　　者：顾剑东 魏超 王志强 李斌 施颖波 周敏 GU Jian-dong;WEI Chao;WANG Zhi-qiang;LI Bin;SHI Ying-bo;ZHOU Min(China Haohua North Paint Industry Research and Design Institute Co.,Ltd.,Lanzhou 730020,China)

机构地区：[1]中昊北方涂料工业研究设计院有限公司,兰州730020

出　　处：《现代涂料与涂装》2021年第12期11-13,共3页Modern Paint & Finishing

摘　　要：通过溶胶-凝胶法制备一种应用于有机玻璃镀膜板表面的高透光率耐磨涂层,研究了MTES与TEOS用量比、硅溶胶的粒径及用量、纳米氧化锌的用量以及树脂的反应条件。结果表明:MTES与TEOS质量比为5∶1,碱性硅溶胶的粒径为12~15 nm,添加量为30%,反应温度控制在78℃左右,反应2 h,可制备出一定透光率的耐磨涂层,通过加入4%的纳米ZnO,可进一步提高涂层透光率。In this paper,a sol-gel method is used to prepare a wear-resistant coating with high light transmittance applied to the surface of PMMA coated plate.The dosage ratio of MTES to TEOS,the particle size and dosage of silica sol,the dosage of nano-ZnO and the reaction conditions of the sol were studied.The results showed that when the mass ratio of MTES to TEOS was 5:1,the particle size of the alkaline silica sol was 12~15 nm,the addition amount was 30%,the reaction temperature was controlled at about 78 ℃,and the reaction time was two hours,a certain amount could be prepared.By adding 4% nano-ZnO,the transmittance of the coating can be further improved.

关 键 词：溶胶-凝胶 硅溶胶 纳米氧化锌 耐磨 高透光率 

分 类 号：TQ633[化学工程—精细化工]