CFRP加工表面粗糙度对力学性能的影响  

Effect of Surface Roughness on Mechanical Behavior of CFRP

作　　者：范文涛 陈燕[1] 陈逸佳 谢松峰 FAN Wentao;CHEN Yan;CHEN Yijia;XIE Songfeng(Jiangsu Key Laboratory of Precision and Micro-manufacturing Technology,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,China)

机构地区：[1]南京航空航天大学江苏省精密与微细制造技术重点实验室,江苏南京210016

出　　处：《机械制造与自动化》2022年第1期27-29,60,共4页Machine Building & Automation

基　　金：国家科技重大专项(2017-Ⅶ-0015-0111);南京航空航天研究生创新基地(实验室)开放基金项目(kfjj20190507)。

摘　　要：选用三维表面算术平均高度Sa表征CFRP的表面粗糙度,以磨削样件的拉伸和压缩强度为标准,研究CFRP多向层合板在不同铣削参数下所产生的加工表面粗糙度对力学性能退化的影响。结果表明:Sa对拉伸强度及压缩强度的影响不显著,Sa>15μm时拉伸强度退化量会增多,加工时温度过高会对CFRP基体造成损伤,进而影响压缩强度。Sa is used to characterize the surface roughness of CFRP,and the tensile and compressive strength of the ground sample is applied as the standard to study the effect of the surface roughness of CFRP multi-directional laminates on the degradation of mechanical properties under different milling parameters.The result shows that effect of Sa on the tensile strength and compressive strength is not evident.When Sa is more than 15μm,the degradation of tensile strength will increase.When the temperature is too high,the CFRP matrix will be damaged and the compressive strength will be affected.

关 键 词：CFRP SA 铣削 拉伸强度 压缩强度 