淬火强度对6005A合金薄壁挤压型材性能影响  

Effect of Quenching Strength on Properties of 6111 Thin Wall Extruded Profiles

作　　者：郝玉喜 徐伍刚 王爽 吴楠 孙巍 HAO Yu-xi;XU Wu-gang;WANG Shuang;WU Nan;SUN Wei(Liaoning Zhongwang Group Co.,Ltd.,Liaoyang Liaoning 111003,China)

机构地区：[1]辽宁忠旺铝合金精深加工有限公司,辽宁辽阳111003

出　　处：《热处理技术与装备》2022年第1期8-11,共4页Heat Treatment Technology and Equipment

基　　金：辽宁省‘兴辽英才计划’项目资助(XLYC1908014)。

摘　　要：对大截面薄壁空腔型材的6005A挤压铝合金采用不同的冷却方式进行固溶处理,采用电子万能试验机和万能研究级倒置式材料显微镜对型材的力学性能、折弯性能和晶粒度进行研究。结果表明,淬火强度提高,则型材的强度提升,同时折弯角度增大,塑性弯曲性能则显著提升。延伸率对折弯性能有一定影响,延伸率越大则塑性越好,折弯角度越大。不同淬火强度对型材基体晶粒度无显著影响,离线淬火型材的皮质层厚度最小。The 6005 A extruded aluminum alloy with large cross-section and thin wall cavity was treated by different quenching cooling methods. The mechanical properties, bending properties and grain size of the profile were studied by electronic universal testing machine and universal research level inverted material microscope. The results showed that with the increase of quenching strength, the mechanical properties of profile increased, the bending angle increased, and the plastic bending property was significantly improved. The elongation had a certain influence on the bending property. The plasticity and bending angle performed better as the elongation improved. The different quenching strength had no significant effect on the grain size of the profile matrix, and the thickness of the cortical layer of the off-line quenched profile was the smallest.

关 键 词：6005A合金 淬火强度 折弯性能 晶粒度 

分 类 号：TG166.3[金属学及工艺—热处理]