高耐磨性复合涂层涤纶通丝的制备及其性能  

Preparation and performance of composite coated polyesterharness cord with high wearability

作　　者：解开放 罗凤香 包新军 周衡书[1,2] 徐广标[3] XIE Kaifang;LUO Fengxiang;BAO Xinjun;ZHOU Hengshu;XU Guangbiao(College of Textile and Fashion, Hunan Institute of Engineering, Xiangtan, Hunan 411104, China;Engineering Technology Research Center of New Fiber Fabric and Processing, Hunan Institute of Engineering, Xiangtan, Hunan 411104, China;College of Textiles, Donghua University, Shanghai 201620, China)

机构地区：[1]湖南工程学院纺织服装学院,湖南湘潭411104 [2]湖南工程学院湖南省新型纤维面料及加工工程技术研究中心,湖南湘潭411104 [3]东华大学纺织学院,上海201620

出　　处：《纺织学报》2022年第3期123-131,共9页Journal of Textile Research

基　　金：湖南省自然科学基金项目(2020JJ4245);湖南省教育厅优秀青年项目(19B129)。

摘　　要：为探索和优化通丝的涂层工艺,并开发出耐磨性优异的通丝,以部分醇解聚乙烯醇(PVA)、水性聚氨酯(PU)和水性环氧树脂(EP)为成膜剂,采用2种方法对编织涤纶通丝进行涂层。一步法采用PVA直接涂层,两步法采用PU/PVA或EP/PVA进行复合涂层。对涂层后通丝进行烘干与热定形处理,对其表观形貌、化学结构、弯曲性能、拉伸性能和耐磨性能进行测试和分析,以评价PU或EP预处理对PVA涂层通丝力学性能的影响。结果表明:PU和EP能够减少PVA涂层与通丝间裂纹的产生,通过在涤纶通丝表面引入极性基团,改善PVA涂层与涤纶间的界面性能;PU/PVA涂层通丝比EP/PVA涂层通丝具有更好的综合性能;经1.5%PU/PVA复合涂层的通丝具有优异的耐磨性能,比PVA涂层通丝的耐磨性提高了135.7%。In order to explore and optimize the coating process of harness cord and develop harness cord for improved wearability,partially alcoholyzed polyvinyl alcohol(PVA),water-based polyurethane(PU)and epoxy resin(EP)were used as film formers,and two methods were used to coat the braided polyester(PET)harness cord.One-step method used PVA for direct coating,and two-step method used PU/PVA or EP/PVA for composite coating.After drying and heat setting,the apparent morphology,chemical structure,bending properties,tensile properties and wearability of coated harness cord were measured and analyzed to evaluate the effect of PU or EP pretreatment on the mechanical properties of PVA coated harness cord.The results show that both PU and EP can reduce the cracks between PVA coating and PET harness cord.By introducing polar groups on the surface of PET harness cord,the interface performance between the PVA coating and the PET fibers is improved.PU/PVA coated harness cord has better comprehensive properties than that of EP/PVA coated harness cord.The 1.5%PU/PVA coated harness cord demonstrates the best wearability,with an increase of 135.7%compared with PVA coated harness cord.

关 键 词：涤纶通丝 复合涂层 聚乙烯醇 聚氨酯 环氧树脂 耐磨性能 提花织机 