High-entropy(La_(0.2)Nd_(0.2)Sm_(0.2)Eu_(0.2)Gd_(0.2))_(2)Ce_(2)O_(7):A potential thermal barrier material with improved thermo-physical properties  

作　　者：Yun XUE Xiaoqin ZHAO Yulong AN Yijing WANG Meizhen GAO Huidi ZHOU Jianmin CHEN 

机构地区：[1]Key Laboratory of Science and Technology on Wear and Protection of Materials,Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences,Lanzhou 730000,China [2]Center of Materials Science and Optoelectronics Engineering,University of Chinese Academy of Sciences,Beijing 100049,China [3]Key Lab for Magnetism and Magnetic Materials of MOE,School of Physical Science and Technology,Lanzhou University,Lanzhou 730000,China

出　　处：《Journal of Advanced Ceramics》2022年第4期615-628,共14页先进陶瓷（英文）

基　　金：This research was financially supported by Youth Innovation Promotion Association(No.2014378)for Chinese Academy of Sciences.The authors are grateful to the constructive comments of the reviewers.

摘　　要：High-entropy oxides(HEOs)are widely researched as potential materials for thermal barrier coatings(TBCs).However,the relatively low thermal expansion coefficient(TEC)of those materials severely restricts their practical application.In order to improve the poor thermal expansion property and further reduce the thermal conductivity,high-entropy(La_(0.2)Nd_(0.2)Sm_(0.2)Eu_(0.2)Gd_(0.2))_(2)Ce_(2)O_(7) is designed and synthesized in this work.The as-prepared multicomponent material is formed in a simple disordered fluorite structure due to the high-entropy stabilization effect.Notably,it exhibits a much higher TEC of approximately 12.0×10^(−6) K^(−1) compared with those of other high-entropy oxides reported in the field of TBCs.Besides,it presents prominent thermal insulation behavior with a low intrinsic thermal conductivity of 0.92 W·m^(−1)·K^(−1) at 1400℃,which can be explained by the existence of high concentration oxygen vacancies and highly disordered arrangement of multicomponent cations in the unique high-entropy configuration.Through high-temperature in-situ X-ray diffraction(XRD)measurement,this material shows excellent phase stability up to 1400℃.Benefiting from the solid solution strengthening effect,it shows a higher hardness of 8.72 GPa than the corresponding single component compounds.The superior thermo-physical performance above enables(La_(0.2)Nd_(0.2)Sm_(0.2)Eu_(0.2)Gd_(0.2))_(2)Ce_(2)O_(7) a promising TBC material.

关 键 词：high-entropy oxides(HEOs) (La_(0.2)Nd_(0.2)Sm_(0.2)Eu_(0.2)Gd_(0.2))_(2)Ce_(2)O_(7) defective fluorite structure thermal expansion coefficient(TEC) thermal conductivity thermal barrier coating(TBC) 

分 类 号：TQ174.1[化学工程—陶瓷工业]