共价有机骨架纳米材料的制备及摩擦学性能研究  

Preparation and Tribological Properties of Covalent Organic Framework Nanomaterials

作　　者：文平 雷永珍 WEN Ping;LEI Yongzhen(Shaanxi Key Laboratory of Phytochemistry,College of Chemistry and Chemical Engineering,Baoji University of Arts and Sciences,Shaanxi Baoji 721013,China)

机构地区：[1]宝鸡文理学院化学化工学院陕西省植物化学重点实验室,陕西宝鸡721013

出　　处：《摩擦学学报》2022年第1期123-130,共8页Tribology

基　　金：国家自然科学基金(51705004);宝鸡文理学院校级重点项目(ZK16056)资助。

摘　　要：利用三聚氯氰和2,5-二氨基-苯并-二噻唑为原料,通过简单的溶剂热法反应制备了一类新型的共价有机骨架纳米材料(简称TTC),该纳米材料具有二维的层状结构,在水和聚乙二醇400(PEG 400)混合润滑体系中呈现出良好的分散性.摩擦学试验表明,添加质量分数为0.5%时,TTC可显著降低钢-钢摩擦对偶上的摩擦系数和磨损体积.摩擦学机制研究表明三嗪环和苯并噻唑环结构高的π电子云密度使TTC与金属铁原子/离子间产生强的相互作用,同时硫原子高的亲合力进一步协同形成稳定的摩擦膜,此外,TTC层间弱的范德华力降低了横向剪切强度,层内共价键保证了润滑膜的力学强度.Covalent organic framework materials are a rising class of two-dimensional layered porous nano-materials,where the atoms in-plane are connected by covalent bonds and van der Waals forces are dominated between the layers.Because of such unique features,covalent organic framework materials have posed a promising potential in lubricant additives.In this work,cyanuric chloride and 2,5-diamino-benzo-dithiazole were served as raw materials,we prepared a novel covalent organic framework nanomaterial(TTC)by a facile solvothermal reaction.The analyses showed that TTC had a good crystallinity and a flexible two-dimensional layered structure with the slight wrinkling.Using water and polyethylene glycol 400 mixed fluid as the base lubricant,when as-synthesized nanomaterials(TTC)introduced into it,a good dispersion could be obtained with the assistance of ultrasonication,due to the formation of hydrogen-bonds between TTC and glycol moieties.Subsequently,the tribological performances of TTC as the additive of mixed fluid,under a load of 100 N,were investigated using an SRV-V friction and wear tester as well as a threedimensional profiler.As the concentration increased,the friction coefficient firstly decreased and then increased.When the addition amount of TTC was up to 0.5%,the friction coefficient(COF)and wear volume of the lower disk can be dramatically reduced(COF reduced by 26%and wear volume decreased by 90%),as compared to that of the control lubricant.Next,the scanning electron microscopy images of the worn surface of the lower disks lubricated with the base fluid and the blends with the different contents of TTC additive were obtained.Lubricated by the base fluid,the worn surface displayed a moderate adhesive and abrasive wear,because of the base fluid with the low viscosity,which hardly produced a stable lubricating film.Besides,under the high load,the direct contact between the asperities on the surface of the friction pair caused a cold weld,then adhesive wear was triggered by the shear moving.TTC can be effectivel

关 键 词：共价有机骨架 润滑添加剂 减摩抗磨性能 摩擦学机制 

分 类 号：TG356.16[金属学及工艺—金属压力加工]