超临界CO_(2)技术下麻织物冰裂纹肌理研究  

Study on ice crack texture of hemp fabric by supercritical CO_(2) technique

作　　者：尚尚 范铁明[1] SHANG Shang;FAN Tie-ming(College of Art and Design,Qiqihar University,Heilongjiang Qiqihar 161006,China)

机构地区：[1]齐齐哈尔大学美术与艺术设计学院,黑龙江齐齐哈尔161006

出　　处：《齐齐哈尔大学学报（自然科学版）》2022年第4期80-82,94,共4页Journal of Qiqihar University(Natural Science Edition)

基　　金：国家社会科学基金项目(19BMZ092);黑龙江省省属高等学校基本科研业务费科研项目(135309322);黑龙江省经济社会发展重点研究课题(20516)。

摘　　要：试验采用分散红54在超临界染色装置上进行亚麻织物的防染印花,探究了染色时间、染色温度、染色压力以及糊料浓度对亚麻织物防染印花性能的影响,测定了染色后亚麻织物及印花的K/S值和色牢度。结果表明,在防染剂质量分数为10%、温度为120℃、压力为20 MPa、染色时间为60 min的条件下,亚麻织物印花防白效果好同时印花能达到最大的K/S值,染色牢度达到4级。The K/S value and color fastness of dyed flax fabric and printing were determined.The results showed that under the conditions of sodium alginate mass fraction 10%,temperature 120℃,pressure 20 MPa and dyeing time 60 min,the flax fabric had good anti-whitening effect and the maximum K/S value,and the dyeing fastness reached grade 3-4,which met the requirements of national standards.

关 键 词：分散染料 防染印花 超临界二氧化碳 亚麻织物 

分 类 号：TS194.449[轻工技术与工程—纺织化学与染整工程]